PURPOSE To investigate and compare the surface roughness (SR), weight and height of monolithic zirconia (MZ), ceramometal (CM), lithium disilicate glass ceramic (LD), composite resin (CR), and their antagonistic human teeth enamel. MATERIALS AND METHODS 32 disc shaped specimens for the four test materials (n=8) and 32 premolars were prepared and randomly divided. SR, weight and height of the materials and the antagonist enamel were recorded before and after subjecting the specimens to 240,000 wear-cycles (49 N/0.8 Hz/5℃/50℃). SR, height, weight, and digital microscopic qualitative evaluation were measured. RESULTS CM (0.23 + 0.08 µm) and LD (0.68 + 0.16 µm) exhibited the least and highest mean difference in the SR, respectively. ANOVA revealed significance ( P =.001) between the materials for the SR. Paired T-Test showed significance ( P <.05) for the pre- and post-SR for all the materials. For the antagonistic enamel, no significance ( P =.987) was found between the groups. However, the pre- and post-SR values of all the enamel groups were significant ( P <.05). Wear cycles had significant effect on enamel weight loss against all the materials ( P <.05). CR and MZ showed the lowest and highest height loss of 0.14 mm and 0.46 mm, respectively. CONCLUSION MZ and CM are more resistant to SR against the enamel than LD and CR. Enamel worn against test materials showed similar SR. Significant variations in SR values for the tested materials (MZ, LD, CM, and CR) against the enamel were found. Wear simulation significantly affected the enamel weight loss against all the materials, and enamel antagonist against MZ and CM showed more height loss.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.