No abstract

No abstract

No abstract

No abstract

Chitosan (CS) nanocomposite mesoporous membranes were fabricated by mixing CS with graphene (G) and fullerene (F) nanofillers, and the diffusion properties through CS membranes were studied. In addition, in order to enhance the binding between the internal CS chains, physical cross-linking of CS by sodium tripolyphosphate (TPP) was carried out. F and G with different weight percentages (0.1, 0.5, and 1 wt.%) were added on physically cross-linked chitosan (CLCS) and non-cross-linked chitosan (NCLCS) membranes by wet mixing. Permeability and diffusion time of CLCS and NCLCS membranes at different temperatures were investigated. The results revealed that the pore size of all fabricated CS membranes is in the mesoporous range (i.e., 2–50 nm). Moreover, the addition of G and F nanofillers to CLCS and NCLCS solutions aided in controlling the CS membranes’ pore size and was found to enhance the barrier effect of the CS membranes either by blocking the internal pores or decreasing the pore size. These results illustrate the significant possibility of controlling the pore size of CS membranes by cross-linking and more importantly the careful selection of nanofillers and their percentage within the CS membranes. Controlling the pore size of CS membranes is a fundamental factor in packaging applications and membrane technology.

No abstract

Fly ash (FA) is produced from coal power plants’ combustion. FA is used in the concrete industry, as an ingredient in the brick and paving. Knowledge of the chemical composition and toxic metal content in FA is essential for evaluating its environmental risks. This study aimed to assess FA purification effect on its antibacterial activity against Escherichia coli and Bacillus cereus, by calculating percent bacterial reduction. Moreover, centrifugation time effect on the purification process was evaluated. Chemical composition and properties of purified FA were determined and compared with raw FA, using Fourier transform Infrared (FTIR); X-ray diffraction (XRD); X-ray photoelectron spectroscopy (XPS); energy-dispersive X-ray (EDXA); carbon, hydrogen, nitrogen, and sulfur (CHNS) elemental analysis; moisture content; and loss-of-ignition. Particle size was predicted by using dynamic laser scattering, BET and scanning electron microscopy (SEM). The CHNS results showed that purified FA contains the highest carbon content (88.9%), as compared to raw FA (82.1%). The particle size distribution (PSD) of FA microspheres ranges from 48.53 ± 17.9 to 52.98 ± 19.4 µm by using SEM. PSD, using dynamic laser scattering, showed polydispersed and non-uniform size in raw FA, ranging in size from 107.1 to 1027 nm, while purified FA manifests a monodispersed size from 103.3 to 127.3 nm. FA showed the least bacterial growth reduction %, while the purified fly ash (FA2) showed the highest bacterial growth reduction %, as compared to the control bacterial broth culture without fly ash.

New three fabricated chitosan (CS) loaded with fly ash (FA) films were developed in this study. The shell waste of white shrimp was used as a precursor for the isolation of chitin and converted into chitosan by carrying out a deacetylation process. The formation of chitosan was conducted by various preparation steps deproteinization, demineralization, and deacetylation. The degree of deacetylation was found to be 95.2%. The obtained chitosan was used to prepare three different chitosan loaded-fly ash films. The prepared films contained various fly ash: chitosan ratios (2:1, FA-CSF1), (1:1, FA-CSF2), and (1:2, FA-CSF3). The obtained films were characterized using FTIR, XRD, and SEM. The micrograph images of the formed films showed spherical particles with an average size of 10 µm. The surface area, adsorption-desorption properties, thermal stability, and water/fat binding features of the fabricated chitosan films were studied. The results revealed that the prepared films displayed typical BET graphs with surface areas ranging from 2.436 m2 g−1 to 8.490 m2 g−1. The fabricated FA-CSF films also showed high thermal stability at temperatures up to 284.9 °C and excellent water/fat binding capacities. The antibacterial potential of the designed films was screened against E. coli (Gram-negative) and B. cereus (Gram-positive) bacterial strains. The tested solution of CS (1%) exhibited inhibition zones for E. coli and B. cereus as 18.51 mm and 14.81 mm, respectively, while in FA solution (1%), the inhibition zones were found to be 10.16 mm, and 13.57 mm, respectively. The results encourage and open up the new and promising areas of research for applying chitosan extracted from waste materials in biological applications.