No abstract

The prevention of root fractures of pulpless teeth is an important clinical issue to maintain healthy teeth through lifetime. The aim of this study was to examine a clinically effective treatment method for strengthening vulnerable pulpless teeth using CAD/CAM (computer-aided design/computer-aided manufacturing) fiber-reinforced post-core by conducting a fracture resistance test. A post-core made with a fiber-reinforced resin disk TRINIA (TR, SHOFU, Kyoto, Japan) was fabricated using a CAD/CAM system. The fiber-layer orientation of the CAD/CAM post-core was parallel to the axis of the restored tooth. A post-core using a conventional composite and a fiber post (CF) was also prepared. A fracture resistance test of teeth restored with the post-cores and zirconia crowns was conducted using a universal testing machine, and fracture patterns were identified by micro-CT observation. The fracture load of the roots restored with TR was 1555.9 ± 231.8 N, whereas that of CF was 1082.1 ± 226.7 N. The fracture load of TR was 43.8% that was significantly higher than that of CF (Student’s t-test, p < 0.05). The restored teeth with CAD/CAM resin post-core were found to be repairable even after fracture. These results suggest that the CAD/CAM indirect fiber post-core has the potential to strengthen the vulnerable pulpless teeth.

Dual-cured resin-based composites are gaining popularity as core build-up materials. Physical and elastoplastic characteristics of new experimental core build-up materials with variable filler contents (+2.5 and +5 wt%) were investigated using classic macroexperiments and nanoindentation. Flexural fracture strength increased from 91.7±11.8 to 114.1±9.1 and 116.6±14.7 MPa in the +2.5 and +5 wt% groups, respectively; similarly, elastic moduli increased from 12.6±0.9 to 15.4±1.2 and 15.3±2.0 MPa, respectively. Fracture toughness increased from 1.82±0.60 to 2.28±0.53 and 2.67±0.88 MPa•m 1/2 for the +2.5 and +5 wt% groups, respectively; indentation hardness increased significantly from 0.45±0.03 to 0.55±0.04 and 0.60±0.10 GPa, respectively. The addition of +5 wt% filler content led to a mechanically superior material; the addition of +2.5 wt% filler led to better reliability.

No abstract