The copolymerization of divinylbenzene (DVB) and N‐isopropylacrylamide (NIPAm) with dimethyl 2,2′‐azobisisobutyrate of a concentration as high as 0.50 mol/L proceeded homogeneously without any gelation at 80 °C in N,N‐dimethylformamide, where the concentrations of DVB and NIPAm were 0.15 and 0.50 mol/L. The copolymer yield increased with time and leveled off over 50 min. Although DVB was consumed more rapidly than NIPAm, both comonomers were completely consumed in 50 min. The homogeneous polymerization system at 80 °C involved electron spin resonance‐observable propagating polymer radicals, the total concentration of which increased with time. The resulting copolymer was soluble in tetrahydrofuran, chloroform, acetone, ethyl acetate, acetonitrile, N,N‐dimethylformamide, dimethyl sulfoxide, and methanol, but insoluble in benzene, n‐hexane, and water. The copolymer showed an upper critical solution temperature (50 °C on cooling) in a methanol–water [11:3 (v/v)] mixture. Dimethyl 2,2′‐azobisisobutyrate fragments as high as 37–45 mol % were incorporated as terminal groups in the copolymers through initiation and primary radical termination. The contents of DVB and NIPAm were 10–30 mol % and 30–50 mol %, respectively. The intrinsic viscosity of the copolymer was very low (0.09 dL/g) at 30 °C in tetrahydrofuran despite high weight‐average molecular weight (1.2 × l06 by multi‐angle laser light scattering). These results indicate that the copolymer was of hyperbranched structure. By transmission electron microscopy observation, the individual copolymer molecules were visualized as nanoparticle of 6–20 nm. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 1609–1617, 2004
ABSTRACT:The homopolymerization of divinylbenzene (DVB) as an excellent crosslinker (0.20 mol/L) with dimethyl 2,2Ј-azobisisobutyrate (MAIB) proceeded homogeneously without any gelation at 80°C in benzene when the MAIB concentrations as high as 0.30 -0.50 mol/L were used, yielding soluble polymers. In the polymerization at the concentrations of [DVB] ϭ 0.20 mol/L and [MAIB] ϭ 0.50 mol/L, the polymer yield increased with time and leveled off over 90 min. The molecular weight and molecular weight distribution increased with polymer yield. The vinyl groups of DVB were observed to be almost completely consumed in about 80 min, by FT near-IR spectroscopic analysis. The homogeneous polymerization system involved ESR-observable polymer radical, the concentration of which increased with time up to 3.4 ϫ 10 Ϫ5 mol/L. The polymer formed in the polymerization for 2 h consisted of 46 mol % of DVB unit and 54 mol % of the methoxycarbonylpropyl group as MAIB fragment, indicating that an initiator-fragment incorporation radical polymerization proceeds in the present polymerization. The polymer was soluble in benzene, tetrahydrofuran, ethyl acetate, chloroform, acetone, and N,N-dimethylformamide, while it was insoluble in n-hexane, acetonitrile, dimethyl sulfoxide, methanol, and water. The results of the multiangle laser light scattering and viscometric measurements revealed that the individual polymer molecules were formed as hyperbranched polymer nanoparticles.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.