This research was devoted to the investigation of changes in structure and properties of a calcium sulfate hemihydrates (CSH) cement immersed in Hanks' solution for different periods of time. XRD patterns indicated a quick phase change (a hydration process) of CSH into calcium sulfate dihydrate (CSD) after the cement powder was mixed with the setting solution. After the hardened cement was immersed in Hanks' solution for 1 d, CSD became the dominant phase. The long-term (up to 30 d) pH value of the Hanks' solution wherein the cement was immersed remained in the range of 67. The hardened cement gradually lost its weight and increased its porosity level with immersion time. When immersed for 1 d, the average compressive strength (CS) value of the cement reached its maximum value. After 30 d, the compressive strength (CS) value of the cement still remained >25 MPa. SEM showed that, after being immersed for 30 d, numerous large, faceted CSD crystals were observed throughout the sample. Cytotoxicity test indicated that the present cement is a biocompatible implant material.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.