The ultimate goal of tissue engineering is to replace damaged tissues by applying engineering technology and the principles of life sciences. To successfully engineer a desirable tissue, three main elements of cells, scaffolds and growth factors need to be harmonized. Biomaterial-based scaffolds serve as a critical platform both to support cell adhesion and to deliver growth factors. Various methods of fabricating scaffolds have been investigated. One recently developed method that is growing in popularity is called electrospinning. Electrospinning is known for its capacity to make fibrous and porous structures that are similar to natural extracellular matrix (ECM). Other advantages to electrospinning include its ability to create relatively large surface to volume ratios, its ability to control fiber size from micro- to nano-scales and its versatility in material choice. Although early work with electrospun fibers has shown promise in the regeneration of certain types of tissues, further modification of their chemical, biological and mechanical properties would permit future advancements. In this paper, current approaches to the development of modular electrospun fibers as scaffolds for tissue engineering are discussed. Their chemical and physical characteristics can be tuned for the regeneration of specific target tissues by co-spinning of multiple materials and by post-modification of the surface of electrospun fibers. In addition, topology or structure can also be controlled to elicit specific responses from cells and tissues. The selection of proper polymers, suitable surface modification techniques and the control of the dimension and arrangement of the fibrous structure of electrospun fibers can offer versatility and tissue specificity, and therefore provide a blueprint for specific tissue engineering applications.

No abstract

BackgroundEnteric Escherichia coli survives the highly acidic environment of the stomach through multiple acid resistance (AR) mechanisms. The most effective system, AR2, decarboxylates externally-derived glutamate to remove cytoplasmic protons and excrete GABA. The first described system, AR1, does not require an external amino acid. Its mechanism has not been determined. The regulation of the multiple AR systems and their coordination with broader cellular metabolism has not been fully explored.ResultsWe utilized a combination of ChIP-Seq and gene expression analysis to experimentally map the regulatory interactions of four TFs: nac, ntrC, ompR, and csiR. Our data identified all previously in vivo confirmed direct interactions and revealed several others previously inferred from gene expression data. Our data demonstrate that nac and csiR directly modulate AR, and leads to a regulatory network model in which all four TFs participate in coordinating acid resistance, glutamate metabolism, and nitrogen metabolism. This model predicts a novel mechanism for AR1 by which the decarboxylation enzymes of AR2 are used with internally derived glutamate. This hypothesis makes several testable predictions that we confirmed experimentally.ConclusionsOur data suggest that the regulatory network underlying AR is complex and deeply interconnected with the regulation of GABA and glutamate metabolism, nitrogen metabolism. These connections underlie and experimentally validated model of AR1 in which the decarboxylation enzymes of AR2 are used with internally derived glutamate.Electronic supplementary materialThe online version of this article (doi:10.1186/s12918-016-0376-y) contains supplementary material, which is available to authorized users.

Tissue engineering has become an alternative method to traditional surgical treatments for the repair of bone defects, and an appropriate scaffold supporting bone formation is a key element in this approach. In the present study, nanofibrous organic and inorganic composite scaffolds containing nano-sized demineralized bone powders (DBPs) with biodegradable poly(L-lactide) (PLA) were developed using an electrospinning process for engineering bone. To assess their biocompatibility, in vitro osteogenic differentiation of human mandible-derived mesenchymal stem cells (hMSCs) cultured on PLA or PLA/DBP composite nanofiber scaffolds were examined. The mineralization of hMSCs cultured with osteogenic supplements on the PLA/DBP nanofiber scaffolds was remarkably greater than on the PLA nanofiber scaffold during the first 14 days of culture but reached the same level after 21 days. The in vivo osteoconductive effect of PLA/DBP nanofibrous scaffolds was further investigated using rats with critical-sized skull defects. Micro-computerized tomography revealed that a greater amount of newly formed bone extended across the defect area in PLA/DBP scaffolds than in the nonimplant and PLA scaffolds 12 weeks after implantation and that the defect size was almost 90% smaller. Therefore, PLA/DBP composite nanofiber scaffolds may serve as a favorable matrix for the regeneration of bone tissue.

We fabricated composite fibrous scaffolds from blends of poly(lactide-co-glycolide) (PLGA) and nano-sized hydroxyapatite (HA) via electrospinning. SEM-EDX and AFM analysis demonstrated that HA was homogeneously dispersed in the nanofibers, and the roughness increased along with the amount of incorporated HA. When hMSCs were cultured on these PLGA/HA composite nanofibers, we found that incorporation of HA on the nanofibers did not affect cell viability whereas increased ALP activity and expression of osteogenic genes as well as the calcium mineralization of hMSCs. Our results indicate that the composite nanofibers can be offered as a potential bone regenerative biomaterial for stem cell based therapies.

This article reviews fundamental and applied aspects of silk–one of Nature’s most intriguing materials in terms of its strength, toughness, and biological role–in its various forms, from protein molecules to webs and cocoons, in the context of mechanical and biological properties. A central question that will be explored is how the bridging of scales and the emergence of hierarchical structures are critical elements in achieving novel material properties, and how this knowledge can be explored in the design of synthetic materials. We review how the function of a material system at the macroscale can be derived from the interplay of fundamental molecular building blocks. Moreover, guidelines and approaches to current experimental and computational designs in the field of synthetic silklike materials are provided to assist the materials science community in engineering customized finetuned biomaterials for biomedical applications.

To successfully develop a functional tissue-engineered vascular patch, recapitulating the hierarchical structure of vessel is critical to mimic mechanical properties. Here, we use a cell sheet engineering strategy with micropatterning technique to control structural organization of bovine aortic vascular smooth muscle cell (VSMC) sheets. Actin filament staining and image analysis showed clear cellular alignment of VSMC sheets cultured on patterned substrates. Viability of harvested VSMC sheets was confirmed by Live/Dead cell viability assay after 24 and 48 h of transfer. VSMC sheets stacked to generate bilayer VSMC patches exhibited strong inter-layer bonding as shown by lap shear test. Uniaxial tensile testing of monolayer VSMC sheets and bilayer VSMC patches displayed nonlinear, anisotropic stress-stretch response similar to the biomechanical characteristic of a native arterial wall. Collagen content and structure were characterized to determine the effects of patterning and stacking on extracellular matrix of VSMC sheets. Using finite-element modeling to simulate uniaxial tensile testing of bilayer VSMC patches, we found the stress-stretch response of bilayer patterned VSMC patches under uniaxial tension to be predicted using an anisotropic hyperelastic constitutive model. Thus, our cell sheet harvesting system combined with biomechanical modeling is a promising approach to generate building blocks for tissue-engineered vascular patches with structure and mechanical behavior mimicking native tissue.

Silk is a natural polymer with broad utility in biomedical applications because it exhibits general biocompatibility and high tensile material properties. While mechanical integrity is important for most biomaterial applications, proper function and integration also requires biomaterial incorporation into complex surrounding tissues for many physiologically relevant processes such as wound healing. In this study, we spin silk fibroin into a protein alloy fibre with whole fibronectin using wet spinning approaches in order to synergize their respective strength and cell interaction capabilities. Results demonstrate that silk fibroin alone is a poor adhesive surface for fibroblasts, endothelial cells, and vascular smooth muscle cells in the absence of serum. However, significantly improved cell attachment is observed to silk-fibronectin alloy fibres without serum present while not compromising the fibres’ mechanical integrity. Additionally, cell viability is improved up to six fold on alloy fibres when serum is present while migration and spreading generally increase as well. These findings demonstrate the utility of composite protein alloys as inexpensive and effective means to create durable, biologically active biomaterials.