Background: With a recurrence rate of over 30%, techniques that offer stronger acromioclavicular (AC) joint reconstruction through increased graft strength may provide longevity. The purpose of our study was to determine the biomechanical strength of a novel tendon graft sutured throughout compared to a native tendon graft in Grade 3 anatomical AC joint reconstruction.
Methods: For this in vitro experiment, nine paired (n = 18) embalmed cadaveric AC joints of three males and six females (age 86 years, range 51–94 years) were harvested. Anatomic repair with fresh bovine Achilles tendon grafts without bone block was simulated. Specimens were divided into two groups; with group 1 using grafts with ultra-high molecular-weight polyethylene (UHMWPE) suture ran throughout the entire length. In group 2, reconstruction with only native allografts was performed. The distal scapula and humerus were casted in epoxy compound and mounted on the mechanical testing machine. Tensile tests were performed using a mechanical testing machine at the rate of 50 mm/min. Maximum load and displacement to failure were collected.
Results: The average load to failure was significantly higher for group 1 compared to group 2, with mean values of 437.5 N ± 160.7 N and 94.4 N ± 43.6 N, (p = 0.001). The average displacement to failure was not significantly different, with 29.7 mm ± 10.6 mm in group 1 and 25 mm ± 9.1 mm in group 2 (p = 0.25).
Conclusion: We conclude that a UHMWPE suture reinforced graft can provide a 3.6 times stronger AC joint reconstruction compared to a native graft.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.