This paper presents the results of a comparative study of methods to prevent the loss of barium during the formation of thin-film proton-conducting electrolyte BaCe0.89Gd0.1Cu0.01O3−δ (BCGCuO) on La2NiO4+δ-based (LNO) cathode substrates by electrophoretic deposition (EPD). Three different methods of the BCGCuO film coating were considered: the formation of the BCGCuO electrolyte film without (1) and with a protective BaCeO3 (BCO) film (2) on the LNO electrode substrate and the formation of the BCGCuO electrolyte film on a modified La1.7Ba0.3NiO4+δ (LBNO) cathode substrate (3). After the cyclic EPD in six stages, the resulting BCGCuO film (6 μm) (1) on the LNO substrate was completely dense, but the scanning electron microscope (SEM) analysis revealed the absence of barium in the film caused by its intensive diffusion into the substrate and evaporation during the sintering. The BCO layer prevented the barium loss in the BCGCuO film (2); however, the protective film possessed a porous island structure, which resulted in the deterioration of the film’s conductivity. The use of the modified LBNO cathode also effectively prevented the loss of barium in the BCGCuO film (3). A BCGCuO film whose conductivity behavior most closely resembled that of the compacts was obtained by using this method which has strong potential for practical applications in solid oxide fuel cell (SOFC) technology.

In this review, recent achievements in the application of high-entropy alloys (HEAs) and high-entropy oxides (HEOs) in the technology of solid oxide fuel cells (SOFC) are discussed for the first time. The mechanisms of the stabilization of a high-entropy state in such materials, as well as the effect of structural and charge factors on the stability of the resulting homogeneous solid solution are performed. An introduction to the synthesis methods for HEAs and HEOs is given. The review highlights such advantages of high-entropy materials as high strength and the sluggish diffusion of components, which are promising for the use at the elevated temperatures, which are characteristic of SOFCs. Application of the medium- and high-entropy materials in the hydrocarbon-fueled SOFCs as protective layers for interconnectors and as anode components, caused by their high stability, are covered. High-entropy solid electrolytes are discussed in comparison with traditional electrolyte materials in terms of conductivity. High-entropy oxides are considered as prospective cathodes for SOFCs due to their superior electrochemical activity and long-term stability compared with the conventional perovskites. The present review also determines the prioritizing directions in the future development of high-entropy materials as electrolytes and electrodes for SOFCs operating in the intermediate and low temperature ranges.