Simultaneous differential scanning calorimetry, DSC, and acoustic emission, AE, measurements were carried out for single crystals of quenched and stress-induced martensite stabilized (SIM-aged) shape memory Ni51Fe18Ga27Co4 alloy. The transformation temperatures were shifted to higher values, the forward (from austenite to martensite) and reverse transitions became sharper and the width of the hysteresis increased in the SIM-aged sample. The energy distributions of acoustic hits showed similar behaviour to those of the quenched sample and the energy exponents, characterizing the power law behaviour, were also similar. For SIM-aged alloys at heating, in accordance with the sharper (burst-like) transition observed in the DSC run, few high-energy solitary hits were observed, and these hits did not fit to the energy distribution function fitted for smaller energies. Thus, these high-energy events were attributed to high sudden jumps in the phase transition during heating. The effect of long-range order (by applying a heat treatment at 573 K for 6 h to transform the B2 austenite to ordered L21 structure) and the SIM-aging on the transformation entropy was also investigated by DSC. It was found that the entropy was about 36% smaller after SIM-aging of the quenched sample and it was practically unchanged after austenite stabilization.

No abstract

Heat treatments of single crystals of Ni44Fe19Ga27Co10 (at.%) shape memory alloys cause various microstructures of the high-temperature phase. The nanodomain structure, consisting of regions of the L21- and B2-phases, and nanosized particles are the main parameters that change during heat treatments and determine the mechanism of nucleation and growth of martensite crystals, the size of thermal-induced martensite lamellae, the temperature Ms, and the temperature intervals of the martensitic transformation. In the as-grown single crystals, the high-temperature phase has only the L21-structure and the MT occurs at low (Ms = 125 K) temperatures due to the motion of the practically single interphase boundary in narrow temperature ranges of 3–7 K. The reduction in the volume fraction of the L21-phase to 40% and the formation of nanodomains (20–50 nm) of the L21-and B2-phases due to annealing at 1448 K for 1 h with quenching causes an increase in the MT temperatures by 80 K. The MT occurs in wide temperature ranges of 40–45 K because of multiple nucleation of individual large (300–500 µm) martensite lamellae and their growth. After aging at 773 K for 1 h, the precipitation of nanosized particles of the ω-phase in such a structure additionally increases the MT temperatures by 45 K. The MT occurs due to the multiple nucleation of packets of small (20–50 μm) martensite lamellae.

No abstract