Comparative investigation of hot cracking sensitivity of commercial welding wires has been performed. It is shown that an all-purpose method of weldability evaluation can be the machine method with controllable forced deformation during TIG welding (PVR-test method), which allows separating the conditions of initiation of solidification cracks and ductility dip cracks in the weld and HAZ metal, and provides comprehensive information about quantitative characteristics of cracking sensitivity. 6 Ref., 9 Figures.
K e y w o r d s : weldability, hot cracks, crack resistance evaluation, high-alloyed steels, nickel alloys
Расчетным методом исследована кинетика напряженно-деформированного состояния при сварке монокристалла никелевого сплава с учетом анизотропии его теплофизических и механических свойств. Показано, что анизотропия свойств монокристалла способствует росту темпа пластических деформаций в температурном интервале ТИх-II по сравнению с изотропным сплавом такого типа (имеющим поликристаллическое строение). В температурном интервале ТИх-II темпы роста продольных пластических деформаций в монокристалле могут примерно в 2,0 2,5 раза превышать таковые в поликристаллическом варианте сплава, что следует учитывать при разработке соответствующих конструкций и технологии их изготовления. Библиогр. 9, табл. 3, рис. 7.
P u b l i s h e d M o n t h l y Si n c e 2 0 0 0 English translation of the monthly « Avtomaticheskaya Svarka» ( Automatic Welding) j ournal published in Russian since 1948 ED I TOR I A L B OA R D Ed i t o r -i n -Ch i e f B . E. P a t o n Su b s c r i p t i o n s , issues per year, air postage and packaging included. B ack issues available.
Разработана методика оценки кратковременных механических свойств сварного соединения «основной-наплавленный металл» трудносвариваемых никелевых жаропрочных сплавов типа ЖС6 при высоких температурах, имитирующего восстановление кромок рабочих лопаток авиационных газотурбинных двигателей при их серийном ремонте. Обоснована, исходя из условия обеспечения технологической прочности такого сварного соединения, необходимость предельного уменьшения по сравнению с действующей нормативно-технической документацией размеров сварных заготовок и образцов для механических испытаний. Разработанная методика опробована на сервогидравлической машине MTS-810 при испытаниях образцов. Она позволила обосновать выбор режимов предварительной термической обработки с целью получения оптимальных прочностных свойств наплавленного металла ЖС6К. Библиогр. 19, табл. 4, рис. 7.
The work deals with multilayer welds made with Inconel 52 wire, which have a high sensitivity to formation of hot ductility dip cracks in the heat-affected zone, and welds made with 52MSS wire, which turned out to be insensitive to formation of this type of cracks at a certain level of strain rates. Changes of structural characteristics of welds made with the above wires were studied by the methods of transmission microscopy, X-ray microprobe analysis, microhardness measurement, as well as electron backscatter diffraction. 9 Ref., 2 Tables, 8 Figures.
The results of evaluation of thermal stressed state in welded joint of nickel alloy Inconel 690 are presented. The experimental-calculation analysis of thermal processes and mathematical modeling of stress-strain state in single-pass welding was performed. The verification of the data by comparing the experimental thermal cycles with the calculated ones showed a good similarity of results of both as to the sizes of a weld as well as to the thermal cycles in the zones at the different distance from the fusion line. The kinetics of stress-strain state in different zones of welded joint was analyzed considering the probability of hot crack formation. It is shown that under the conditions of modeling linear one-pass welding of plates of 3 mm thickness with energy input of 304 J/mm the arising stresses and deformations do not exceed the critical values and, at the same time do not create the conditions for hot crack formation. The applied mathematical model can be used in evaluation of kinetics of stress-strain state for different variants of welding (change in energy input, different filler material, etc.). 7 Ref., 1 Table, 5 Figures.
K e y w o r d s : nonconsumable-electrode arc welding, nickel alloys, thermal processes, thermal cycles, mathematical modeling, stresses, deformationsThe nickel-based alloys play an important role as corrosion-resistant materials in the nuclear and chemical industries, especially under conditions of operation at the high temperatures, considerable stresses and aggressive environments. The widely used nickel-based alloys at the present time are alloys of Ni-Cr-Fe alloying system. One of such alloys is Inconel 690 with high chromium content (30 %) [1]. The welded joints of Inconel 690 with appropriate filler materials showed a high sensitivity to hot crack formation, particularly under the conditions of welding of thick-walled structural elements. The alloys manifest the highest tendency to the formation of ductility-dip cracks [2,3].As was shown previously [4], the ductility-dip cracks in welding of alloys of alloying system Ni-Cr-Fe occur at the temperature range of 1050-650 °C, the value of critical deformation of crack formation ε cr is about 1.2 %.The thermal processes in fusion welding have a decisive influence on the nature and kinetics of changes in the stress-strain state, structure and properties of weld and HAZ. In this regard, the analysis of temperature fields in welding of alloys of Ni-Cr-Fe alloying system with the aim of further investigations of kinetics of stress-strain state and evaluation of tendency to hot crack formation is an urgent problem.The aim of the work was a comparative experimental and calculation analysis of temperature fields and modeling of stress-strain state in one-pass argon-arc welding of alloy Inconel 690.The computer prediction and calculation allow determining the temperature fields for different values of thermal power of the arc. Using the calculation procedure the efficiency coefficient of the arc is established, which varies depending on the ...
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.