The techniques of x-ray diffraction, x-ray photoelectron spectroscopy (XPS), Auger analysis, and transmission and scanning transmission electron microscopy (TEM) have been applied to the analysis of thin films of Pb(Zr0.30Ti0.70)O3 (PZT30/70) deposited at low temperatures (510 °C) by a sol–gel process onto Pt/Ti electrodes on SiO2/Si 100 substrates. It is found that the platinum film is highly oriented with the [111] axis perpendicular to the substrate plane. The ferroelectric film tends to crystallize epitaxially upon this as columnar crystals. There are indications from the TEM of the existence of a second metallic phase at the interface between the platinum and the PZT30/70 film, which may be associated with its nucleation. The TEM shows the boundaries between the individual sol–gel layers, although the growing crystallites of the PZT30/70 propagate through these boundaries unhindered. The XPS and Auger analyses have shown that Pb penetrates through the Pt layer to the underlying Ti layer, even at the low crystallization temperatures used. There is also clear evidence for diffusion of the Zr and Ti prior to, or during the crystallization process, so that the Zr migrates to the surface of each sol–gel layer. The effects of using different crystallization processes on this compositional separation and the reasons for its occurrence are discussed, as are the possible effects upon macroscopically measured ferroelectric properties.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.