Electrical control of magnetic properties is crucial for device applications in the field of spintronics. Although the magnetic coercivity or anisotropy has been successfully controlled electrically in metals as well as in semiconductors, the electrical control of Curie temperature has been realized only in semiconductors at low temperature. Here, we demonstrate the room-temperature electrical control of the ferromagnetic phase transition in cobalt, one of the most representative transition-metal ferromagnets. Solid-state field effect devices consisting of a ultrathin cobalt film covered by a dielectric layer and a gate electrode were fabricated. We prove that the Curie temperature of cobalt can be changed by up to 12 K by applying a gate electric field of about ±2 MV cm(-1). The two-dimensionality of the cobalt film may be relevant to our observations. The demonstrated electric field effect in the ferromagnetic metal at room temperature is a significant step towards realizing future low-power magnetic applications.

The spin transfer torque is essential for electrical magnetization switching. When a magnetic domain wall is driven by an electric current through an adiabatic spin torque, the theory predicts a threshold current even for a perfect wire without any extrinsic pinning. The experimental confirmation of this 'intrinsic pinning', however, has long been missing. Here, we give evidence that this intrinsic pinning determines the threshold, and thus that the adiabatic spin torque dominates the domain wall motion in a perpendicularly magnetized Co/Ni nanowire. The intrinsic nature manifests itself both in the field-independent threshold current and in the presence of its minimum on tuning the wire width. The demonstrated domain wall motion purely due to the adiabatic spin torque will serve to achieve robust operation and low energy consumption in spintronic devices.

Magnetic and electric properties of transition-metal-doped ZnO films Appl. Phys. Lett. 79, 988 (2001); 10.1063/1.1384478Effect of growth temperature on Curie temperature of magnetic ultrathin films Co/Cu (100) Temperature-dependent magnetism in transition metal films observed by magnetic force microscopy and classical magnetometry

Controlling the displacement of a magnetic domain wall is potentially useful for information processing in magnetic non-volatile memories and logic devices. A magnetic domain wall can be moved by applying an external magnetic field and/or electric current, and its velocity depends on their magnitudes. Here we show that the applying an electric field can change the velocity of a magnetic domain wall significantly. A field-effect device, consisting of a topgate electrode, a dielectric insulator layer, and a wire-shaped ferromagnetic Co/Pt thin layer with perpendicular anisotropy, was used to observe it in a finite magnetic field. We found that the application of the electric fields in the range of ± 2-3 mV cm − 1 can change the magnetic domain wall velocity in its creep regime (10 6 -10 3 m s − 1 ) by more than an order of magnitude. This significant change is due to electrical modulation of the energy barrier for the magnetic domain wall motion.

The current-induced effective field in perpendicularly magnetized Ta/CoFeB/MgO wire was investigated. A threshold field decrease of 6.4 kOe/mA was observed by measuring the threshold field of Hall resistance versus the magnetic field curve with various bias currents. The decrease was probably caused by the in-plane effective field, mainly due to the Rashba effect. The effective field of the Ta/CoFeB/MgO wire was smaller and opposite in direction compared to that of Pt/Co/AlOx previously reported.