In this work, we correlate network dynamics, supramolecular reversibility and the macroscopic surface scratch healing behavior for a series of elastomeric ionomers based on an amorphous backbone with varying fractions of carboxylate pendant groups completely neutralized by Na(+), Zn(2+) or Co(2+) as the counter ions. Our results based on temperature dependent dynamic rheology with simultaneous FTIR analysis clearly indicate that the effective supramolecular bond lifetime (τ(b)) is an important parameter to ascertain the ideal range of viscoelasticity for good macroscopic healing. The reversible coordination increased with higher valence metal ions and ionic content. Both rheological and spectroscopic analyses show a decrease in supramolecular assembly with temperature. The temperature dependent τ(b) was used to calculate the activation energy (Ea) of dissociation for the ionic clusters. According to self-healing experiments based on macroscale surface scratching, a supramolecular bond lifetime between 10 and 100 s results in samples with complete surface scratch healing and good mechanical robustness.

While it is traditionally accepted that the chain interactions responsible for the elastic response in an elastomeric network are ideally permanent and instantaneously active, the ongoing investigation of self-healing materials reveals that the introduction of self-healing properties into elastomers requires high mechanical integrity under dynamic load conditions, while on long timescales (or at extended temperatures), the chain and bond dynamics must allow for an intrinsic repair of micro cracks occurring during operation and aging. Based on an acrylate-based amorphous ionomer model system with pendant carboxylate groups allowing the systematic variation of the composition and the nature of the counter ion, we demonstrate the interrelation between the morphological, thermal, and mechanical properties, and identify the prerequisites and tools for property adjustment and optimization of self-healing efficiency. While the ion fraction is directly related to the effective network density and elastic performance, the crossover frequency between viscous and elastic behavior is influenced by the nature of the counter ion. In order to achieve reliable elastic response and optimal damage repair, the ion fraction in these systems should be in the range of 5 mol% and the chain dynamics should be appropriate to allow for excellent self-healing behavior at moderate healing temperatures.

No abstract

No abstract

No abstract