Low-pressure cold gas dynamic spraying was used to deposit WC-4wt%Ni and WC-4wt%Ni-1wt%Mo coatings onto mild steel. Dense coatings with very low porosities were produced. No decarburization occurred during deposition and no deleterious phases were formed. The coatings were subjected to standardized material characterization tests, as well as slurry abrasion testing to assess their wear behaviour. The wear tests were conducted in synthetic minewater-silica slurries, while distilled watersilica slurries were used as a control. The hardness of the coatings, 512HV 0.3 and 458HV 0.3 for WC-4wt%Ni and WC-4wt%Ni-1wt%Mo respectively, are comparable to those achieved using high-temperature coating processes. The abrasion wear rates for both coatings were less than 5 mg/min and 10 mg/min in the distilled water-silica and synthetic mine water-silica slurries respectively. The approximately 50% increase in wear rate in the synthetic minewater slurry is attributed to a synergistic corrosive wear mechanism. The predominant wear mechanisms were identified as binder smearing and delamination, with carbide grain fracture and pull-out. tungsten carbide, nickel, cold spray, coatings, abrasion, minewater.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.