This study investigated the potentiodynamic corrosion behavior of carbon fiber reinforced plastic (CFRP) and automotive rolled mild steel alloy (SPCC alloy) under different surface roughness conditions. Electrochemical characterization was performed using a potentiodynamic corrosion test with 5.0 wt.% NaCl aqueous solution at 25 ± 2 °C, while microstructural and compositional changes before and after corrosion were evaluated using field emission scanning electron microscopy (FE-SEM) and energy dispersive spectroscopy (EDS), respectively. The CFRP and SPCC corrosion rate increased as surface roughness increased. Generally, SPCC corroded faster than CFRP. The surface composition of CFRP was not affected by corrosion, regardless of the surface roughness conditions. Conversely, SPCC exhibited remarkable changes due to the formation of oxides, and its corrosion was more severe than that of CFRP as surface roughness increased. We used a double flat electrode cell to conduct a galvanic corrosion test in this study at 25 ± 2 °C. In this galvanic corrosion test, we studied different kinds of surface roughness for SPCC specimens under the CFRP material in its as-received condition and #200 condition. We confirmed that the results of galvanic corrosion for this study have a difference in corrosion amount and corrosion rate of SPCC specimens according to the surface roughness of CFRP.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.