The loss of mechanical properties in heat treatable aluminum alloys categories during arc fusion welding processes is a critical issue, which limits the direct application in contrast to different post-treatments methods. This work involved a strategy for the novel and distinctive formation of fillers using 3-mm-diameter (AA6061) tubes having MWCNTs and TiO 2 nanoparticles coating on the inner surface. A series of experiments were conducted using TIG welding to evaluate the effect of welding current and composition of inside coating (MWCNTs-TiO 2) contents on welding strength. Three gradually increasing current values (160 A, 180 A and 200 A) were selected and tested against three combinations of nanocomposite coatings that include 1 wt% MWCNTs-TiO 2 , 1.5 wt% MWCNTs-TiO 2 and 2 wt% MWCNTs-TiO 2. Acceptable qualified bonding between nanocomposite and inside surface is utmost important before conducting the experiments, Tape Test (ASTM-D3359-09 e2) was performed for the assessment of bonding conditions and led to qualitatively exceptional bonding conditions after applying vacuum heating cycle. Tensile test results have demonstrated a significant improvement of 34.20-45.65% strength using innovative nanocomposite coated semi-sectioned tube in comparison to tube fillers without coating. Meanwhile, a beneficial gradually forming W-shape microhardness profile in contrast to conventional U and V shape profiles was achieved at 1.5 and 2 wt% of MWCNTs, and the uplift of hardness in the WZ region up to 86.51% subjected to increase high MWCNTs contents in combination with the current. Therefore, it is concluded to be a virtuous strategy for reinforcing mechanism of weldments to encounter some fusion property loss in aluminum alloys.

No abstract

No abstract

No abstract

No abstract