Mode I interlaminar fracture toughness was evaluated and fracture surfaces were observed to investigate crack propagation behaviors and establish the relationship between fracture toughness and fracture surface morphology in multidirectional carbon fiber/epoxy composites. Double cantilever beam specimens, with artificial cracks made of Teflon film embedded in the middle plane, were prepared. Six crack lengths were considered (25-50 mm). The slopes of the load displacement curves depend on the initial crack length. The mode I interlaminar fracture toughness at crack initiation is approximately constant, regardless of the initial crack length, but fluctuates with crack propagation.
The fracture surface morphology indicates that the R-curve is closely related to the crack propagation mechanism.The fracture surface exhibits damage, such as crack migration, fiber bridging, crack branching, double cracking, and ply splits. These results provide insight into interlaminar fracture toughness assessment and the crack propagation behavior of multidirectional carbon fiber/epoxy composites.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.