This work presents the influence of post processing on morphology, thermal and electrical properties of indium tin oxide (ITO) thin films annealed at 400 °C in different atmospheres. The commercially available 170 nm thick ITO layers deposited on glass were used as a starting material. The X-ray diffraction measurements revealed polycrystalline structure with dominant signal from (222) plane for all samples. The annealing reduces the intensity of this peak and causes increase of (221) and (440) peaks. Atomic force microscopy images showed that the surface morphology is typical for polycrystalline layers with roughness not exceeding few nm. Annealing in the oxygen and the nitrogen-hydrogen mixture (NHM) changes shapes of grains. The electrical conductivity decreases after annealing except the one of layer annealed in NHM. Thermal conductivities of annealed ITO thin films were in range from 6.4 to 10.6 W·m−1·K−1, and they were higher than the one for starting material—5.1 W·m−1·K−1. Present work showed that annealing can be used to modify properties of ITO layers to make them useful for specific applications e.g., in ITO based solar cells.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.