Background Skin burn wound is a notable medical burden worldwide. Rapid and effective treatment of burnt skin is vital to fasten wound closure and healing properly. Amniotic graft and Aloe vera are widely used as wound managing biomaterials. Sophisticated processing, high cost, availability, and the requirement of medics for transplantation limit the application of amnion grafts. We aim to prepare a novel gel from amnion combined with the Aloe vera extract for burn wound healing which overcome the limitations of graft. Methods Two percent human amniotic membrane (AM), Aloe vera (AV) and AM+AV gels were prepared. In vitro cytotoxicity, biocompatibility, cell attachment, proliferation, wound healing scratch assays were performed in presence of the distinct gels. After skin irritation study, second-degree burns were induced on dorsal region of Wistar rats; and gels were applied to observe the healing potential in vivo. Besides, macroscopical measurement of wound contraction and re-epithelialization; gel treated skin was histologically investigated by Hematoxylin and eosin (H&E) staining. Finally, quantitative assessment of angiogenesis, inflammation, and epithelialization was done. Results The gels were tested to be non-cytotoxic to nauplii and compatible with human blood and skin cells. Media containing 500 μg/mL AM+AV gel were observed to promote HaCaT and HFF1 cells attachment and proliferation. In vitro scratch assay demonstrated that AM+AV significantly accelerated wound closure through migration of HaCaT cells. No erythema and edema were observed in skin irritation experiments confirming the applicability of the gels. AV and AM+AV groups showed significantly accelerated wound closure through re-epithelialization and wound contraction with P < 0.01. Macroscopically, AM and AM+AV treated wound recovery rates were 87 and 90% respectively with P < 0.05. Histology analysis revealed significant epitheliazation and angiogenesis in AM+AV treated rats compared to control ( P < 0.05). AM+AV treated wounds had thicker regenerated epidermis, increased number of blood vessels, and greater number of proliferating keratinocytes within the epidermis. Conclusion We demonstrated that a gel consisting of a combination of amnion and Aloe vera extract has high efficacy as a burn wound healing product. Amniotic membrane combined with the carrier Aloe vera in gel format is easy to produce and to apply.

Nitrification can increase levels of soluble lead in potable water by reducing pH. The magnitude of the pH drop depends on the initial alkalinity and extent of nitrification. At 100 mg/L alkalinity as CaCO3, complete nitrification did not significantly decrease pH (pH stayed >7.5) or increase lead contamination of water for lead pipe, but at 15 mg/L alkalinity, nitrification decreased the pH by 1.5 units (pH reduced to <6.5) and increased soluble lead contamination by 65 times. Lower pH values from nitrification also leached 45% more lead and 81% more zinc from leaded brass connected to PVC pipes relative to the same situation for copper pipes. Particulate lead leaching was high but did not vary dependent on nitrification. While nitrification also produces nitrite and nitrate and reduces inorganic carbon and dissolved oxygen, these factors did not significantly impact lead leaching in this work.

Methane cracking on a 5-wt% Ni/c-Al 2 O 3 was studied in a thermobalance. Results showed that the faster rates for carbon deposition obtained at high temperatures (600-650°C) are accompanied by faster deactivation. A similar trend was observed for lower initial masses of catalyst (0.1-0.2 g). Finally, a method of partial gasification was proposed as a promising route for catalyst regeneration.

Indigenous drinking water organisms were used to establish nitrification in glass reactors containing copper or polyvinyl chloride (PVC) surfaces. The reactors were fed soil-derived humics as the organic carbon source and ammonium sulfate as the nitrogen source in biologically treated tap water. Water in the reactors was stagnant for 8 h and then flowed for 5 min to simulate conditions in household plumbing. Following the establishment of complete nitrification (conversion of ammonia to nitrate) in both reactor types, various inhibitors of nitrification were tested followed by a period where recovery of nitrification was observed. In one PVC reactor, copper was gradually introduced up to 1.3 ppm. To ensure that most of the copper was in the ionic form, the pH of the influent was then gradually lowered to 6.6. No significant change in nitrification was observed in the presence of copper. Chlorite was introduced into copper and PVC reactors at doses increasing from 0.2 ppm to 20 ppm. There was limited effect on the PVC system and inhibition in the copper reactor only at 20 ppm. Chloramine was tested at chlorine to ammonia ratios ranging from 0.5:1 to 5:1. Nitrification activity was impacted significantly at a 5:1 ratio and ultimately stopped, with the fastest response being in the copper system. Whenever a control mechanism was tested, there was increased release of copper from the reactors with copper coupons. In all cases, nitrification recovered when inhibitors were removed but the rates of recovery differed depending on the treatment method and coupon surface.