Polyaniline@graphene/nickel oxide (Pani@GN/NiO), polyaniline/graphene (Pani/GN), and polyaniline/nickel oxide (Pani/NiO) nanocomposites and polyaniline (Pani) were successfully synthesized and tested for ammonia sensing. Pani@GN/NiO, Pani/NiO, Pani/GN, and Pani were characterized using X-ray diffraction, UV–vis spectroscopy, Raman spectroscopy, scanning electron microscopy, and transmission electron microscopy. The as-prepared materials were studied for comparative dc electrical conductivity and the change in their electrical conductivity on exposure to ammonia vapors followed by ambient air at room temperature. It was observed that the incorporation of GN/NiO in Pani showed about 99 times greater amplitude of conductivity change than pure Pani on exposure to ammonia vapors followed by ambient air. The fast response and excellent recovery time could probably be ascribed to the relatively high surface area of the Pani@GN/NiO nanocomposite, proper sensing channels, and efficaciously available active sites. Pani@GN/NiO was observed to show better selectivity toward ammonia because of the comparatively high basic nature of ammonia than other volatile organic compounds tested. The sensing mechanism was explained on the basis of the simple acid–base chemistry of Pani.

No abstract

No abstract

Polypyrrole (PPy) and polypyrrole/cerium oxide nanocomposite (PPy/CeO2) were prepared by the chemical oxidative method in an aqueous medium using anhydrous ferric chloride (FeCl3) as an oxidant. The successful formulation of materials was confirmed by Fourier transform infrared spectroscopy (FT-IR), X-ray diffraction (XRD), thermogravimetric analysis (TGA), scanning electron microscopy (SEM), and transmittance electron microscopy (TEM). A four-in-line probe device was used for studying DC electrical conductivity and ammonia vapor sensing properties of PPy and PPy/CeO2. The significant improvement in both the conductivity and sensing parameters of PPy/CeO2 compared to pristine PPy reveals some synergistic/electronic interaction between PPy and cerium oxide nanoparticles (CeO2 NPs) working at molecular levels. The initial conductivity (i.e., conductivity at room temperature) was found to be 0.152 Scm−1 and 1.295 Scm−1 for PPy and PPy/CeO2, respectively. Also, PPy/CeO2 showed much better conductivity retention than pristine PPy under both the isothermal and cyclic ageing conditions. Ammonia vapor sensing was carried out at different concentration (0.01, 0.03, 0.05, 0.1, 0.2, 0.3, 0.4, and 0.5 vol %). The sensing response of PPy/CeO2 varied with varying concentrations. At 0.5 vol % ammonia concentration, the % sensing response of PPy and PPy/CeO2 sensor was found to be 39.1% and 93.4%, respectively. The sensing efficiency of the PPy/CeO2 sensor was also evaluated at 0.4. 0.3, 0.2, 0.1, 0.05, 0.03, and 0.01 vol % ammonia concentration in terms of % sensing response, response/recovery time, reversibility, selectivity as well as stability at room temperature.

No abstract

No abstract

No abstract

No abstract