This paper investigates the root cause of a failure in gas-turbine blades, made of Nimonic-105 nickel-based superalloy. The failure was reported in two blades in the second stage of a turbine-compressor of a gas turbine in the hot section. Two failed blades were broken from the root and from the airfoil. The failure took place after 20 k h of service exposure in the temperature range 700–850 °C, with the rotating speed being in the range 15,000–16,000 rpm. The microstructures of the failed blades were studied using optical/electron microscopes. Energy dispersive X-ray spectroscopy (EDS) was employed for phase identification. Results showed that failure first initiated from the root. The dominant failure mechanism in the root was concluded to be corrosion-fatigue. The failure scenario was suggested based on the results obtained.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.