Lawsonia inermis also known as henna was studied as a corrosion inhibitor for aluminum alloy in seawater. The inhibitor has been characterized by optical study via Fourier transform infrared spectroscopy (FTIR). The FTIR proves the existence of hydroxyl and carbonyl functional groups in Lawsonia inermis. Aluminum alloy 5083 immersed in seawater in the absence and presence of Lawsonia inermis was tested using electrochemistry method, namely, electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization (PP). EIS and PP measurements suggest that the addition of Lawsonia inermis has caused the adsorption of inhibitor on the aluminum surface. The adsorption behavior of the inhibitor follow Langmuir adsorption model where the value of free energy of adsorption, -ΔG, is less than 40 kJ/mol indicates that it is a physical adsorption. Finally, it was inferred that Lawsonia inermis has a real potential to act as a corrosion inhibitor for aluminum alloy in seawater.
Abstract. The investigation of coating incorporated with various percentages of henna has been conducted by means of weight loss, potentiodynamic polarization and electrochemical impedance spectroscopy method. Mild steel has been studied at ambient temperature and 50°C in order to examine the effect of temperature. The potentiodynamic polarization measurements indicate that henna extract acts as a mixed inhibitor while the corrosion rate (CR) value decreases as the current density (I corr ) decreases in the presence of 10% henna extract for both temperatures. Surface and protective film analysis have been carried out using Fourier transform infrared (FTIR) and scanning electron microscopy (SEM).The inhibition activity is mainly correlated with the major active functional groups of lawsone. The main components can be found in lawsone structures are phenols O-H, carboxylic acid C=O and alkenes C=C. The morphology of the uninhibited sample showsa rough surface of mild steel as a result of corrosion process and severe damage can be seen. In the presence of henna, a smooth surface of mild steel anda uniform deposition of henna were observed.
The corrosion performance of aluminum alloy 5083 (AA5083) was investigated in the splash zone area simulated in salt spray cabinet at ambient temperature. Three paint formulations were prepared in accordance with different percentages of henna extract. FTIR method was used to determine the constituent of henna while weight loss and electrochemical method were applied to investigate the inhibition behaviour. The findings show that corrosion rate of aluminum alloy decreased with the increases of henna extract in the coating formulation. The rise of charge transfer resistance (Rct) value has contributed to the greater protection of the coated aluminum. The decrease in double layer capacitance value (Cdl) is another indicator that a better protective barrier has been formed in the presence of henna in the coating matrix.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.