A novel approach of a gas pressure infiltration technique is presented for the synthesis of Co-Continuous Ceramic Composite (C4). SiC foams of varying pore sizes were infiltrated with aluminium AA5083. Optical examination revealed that the SiC foams contained open cells with a network of triangular voids. The number of pores-per-inch (PPI) in the foams was found to depend on the strut thickness and pore diameter. The compressive strengths of two foam configurations, 10 and 20 PPI, were estimated to lie between 1–2 MPa. After infiltration, the compressive yield strength of the resulting C4 was observed to increase to 126 MPa and 120 MPa, respectively, for the 10 and 20 PPI C4. Additionally, the infiltration of ceramic foam with the AA5083 alloy resulted in an increase in strength of 58–100 times when compared with plain ceramic foam. The failure modes of the composites in compression were analyzed by crack propagation and determining the type of failure. The study revealed that shear failure and vertical splitting were the predominant mechanisms of compression failure, and that the fabricated C4 is advantageous in mechanical properties compared to the plain ceramic foam. This study, therefore, suggests the use of C4 composites in armour applications.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.