In this study, nanocrystalline cellulose (NCC) was produced with different concentrations of hydrochloric acid (HCl) and its surface charge, particle size, crystallinity and thermal properties were assessed. The obtained NCC was then used as reinforcement agent in nitrile butadiene rubber (NBR) composites. The NCC was found to have a particle size less than 100 nm, with surface charge ranging from -0.697 mV to -14.8 mV. The crystallinity index decreased to 64.78% for the NCC obtained with 6M HCl. The NCC synthesized with 1M HCl showed the highest thermal stability, as demonstrated by TGA and DSC results. TEM analysis revealed that the NCC obtained with 5M HCl had the smallest particle size. The addition of different amounts of NCC into nitrile butadiene rubber (NBR) composites led to an enhancement of mechanical properties in terms of tensile strength, modulus and elongation at break up to the loading of 5 phr, but no substantial improvement in tear strength was noticed.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.