No abstract

No abstract

Background Three-dimensional (3D) spheroid culture can promote the osteogenic differentiation of bone marrow mesenchymal stromal cells (BMSC). 3D printing offers the possibility to produce customized scaffolds for complex bone defects. The aim of this study was to compare the potential of human BMSC cultured as 2D monolayers or 3D spheroids encapsulated in constructs of 3D-printed poly-L-lactide-co-trimethylene carbonate scaffolds and modified human platelet lysate hydrogels (PLATMC-HPLG) for bone regeneration. Methods PLATMC-HPLG constructs with 2D or 3D BMSC were assessed for osteogenic differentiation based on gene expression and in vitro mineralization. Subsequently, PLATMC-HPLG constructs with 2D or 3D BMSC were implanted in rat calvarial defects for 12 weeks; cell-free constructs served as controls. Bone regeneration was assessed via in vivo computed tomography (CT), ex vivo micro-CT and histology. Results Osteogenic gene expression was significantly enhanced in 3D versus 2D BMSC prior to, but not after, encapsulation in PLATMC-HPLG constructs. A trend for greater in vitro mineralization was observed in constructs with 3D versus 2D BMSC (p > 0.05). In vivo CT revealed comparable bone formation after 4, 8 and 12 weeks in all groups. After 12 weeks, micro-CT revealed substantial regeneration in 2D BMSC (62.47 ± 19.46%), 3D BMSC (51.01 ± 24.43%) and cell-free PLATMC-HPLG constructs (43.20 ± 30.09%) (p > 0.05). A similar trend was observed in the histological analysis. Conclusion Despite a trend for superior in vitro mineralization, constructs with 3D and 2D BMSC performed similarly in vivo. Regardless of monolayer or spheroid cell culture, PLATMC-HPLG constructs represent promising scaffolds for bone tissue engineering applications.

No abstract

No abstract

Mandibular osteomyelitis (OM) is a challenging disease. Our objective was to assess a new OM model in rabbits induced by arsenic trioxide and to assess the efficacy of local treatment of OM using injectable gentamicin‐collagen hydrogels (GNT‐COLL). OM was induced unilaterally by controlled confinement of arsenic trioxide paste to the root canal of lower incisors of rabbits, while OM progression was characterized for 16 weeks. On the other hand, two injectable COLL hydrogels functionalized with GNT were prepared and characterized for physicochemical properties; a simple GNT‐COLL and a nanohydroxyapatite (nHA)‐ loaded hydrogel (GNT‐COLL/nHA). The two hydrogels were evaluated to treat OM model, while a multidose intramuscular GNT solution served as positive control. Outcomes were assessed by standard methods at 4 and 12 weeks post‐surgery. The clinical, radiographical, and histopathological findings provided evidence for the validity of the arsenic‐induced OM. The results demonstrated that a single intra‐lesional injection of the two hydrogels was more suppressive to OM compared to multidose systemic GNT. The composite GNT‐COLL/nHA hydrogel proved to induce early preservation of alveolar bone (ridge) length and higher amount of bone area\total area at 4 weeks (40.53% ± 2.34) followed by GNT‐COLL (32.21% ± 0.72). On the other hand, the positive control group revealed the least ridge length and bone area\total area (26.22% ± 1.32) at 4 weeks. Both hydrogels successfully arrested OM with no signs of recurrence for up to 12 weeks. Therefore, results support the greater advantages of the composite hydrogel as an osteogenic/antibiotic delivery system in OM treatment.

Three-dimensional (3D) spheroid culture can promote the osteogenic differentiation and bone regeneration capacity of mesenchymal stromal cells (MSC). Gingiva-derived progenitor cells (GPC) represent a less invasive alternative to bone marrow MSC (BMSC) for clinical applications. The aim of this study was to test the in vivo bone forming potential of human GPC and BMSC cultured as 3D spheroids or dissociated cells (2D). 2D and 3D cells encapsulated in constructs of human platelet lysate hydrogels (HPLG) and 3D-printed poly (L-lactide-co-trimethylene carbonate) scaffolds (HPLG-PLATMC) were implanted subcutaneously in nude mice; cell-free HPLG-PLATMC constructs served as a control. Mineralization was assessed using micro-computed tomography (µCT), histology, scanning electron microscopy (SEM) and in situ hybridization (ISH). After 4–8 weeks, µCT revealed greater mineralization in 3D-BMSC vs. 2D-BMSC and 3D-GPC (p < 0.05), and a similar trend in 2D-GPC vs. 2D-BMSC (p > 0.05). After 8 weeks, greater mineralization was observed in cell-free constructs vs. all 2D- and 3D-cell groups (p < 0.05). Histology and SEM revealed an irregular but similar mineralization pattern in all groups. ISH revealed similar numbers of 2D and 3D BMSC/GPC within and/or surrounding the mineralized areas. In summary, spheroid culture promoted ectopic mineralization in constructs of BMSC, while constructs of dissociated GPC and BMSC performed similarly. The combination of HPLG and PLATMC represents a promising scaffold for bone tissue engineering applications.

No abstract