The European beech (Fagus sylvatica L.) wood was thermally modified in the presence of paraffin at the temperatures of 190 or 210 °C for 1, 2, 3 or 4 h. A significant increase in its resistance to the brown-rot fungus Poria placenta (by 71.4%–98.4%) and the white-rot fungus Trametes versicolor (by 50.1%–99.5%) was observed as a result of all modification modes. However, an increase in the resistance of beech wood surfaces to the mold Aspergillus niger was achieved only under more severe modification regimes taking 4 h at 190 or 210 °C. Water resistance of paraffin-thermally modified beech wood improved—soaking reduced by 30.2%–35.8% and volume swelling by 26.8%–62.9% after 336 h of exposure in water. On the contrary, its mechanical properties worsened—impact bending strength decreased by 17.8%–48.3% and Brinell hardness by 2.4%–63.9%.
In Central Europe, European beech (Fagus sylvatica L.) wood has a high potential for the production of construction and decorative materials, with the aim of replacing Norway spruce, oaks, and other traditionally used tree species. However, the biological resistance of beech wood—to decaying fungi, molds, and insects—is low, and in damp conditions its resistance must be increased with suitable preservatives or modification methods. In the present experiment, beech wood was first treated with water systems of nano-zinc oxide (0.1 to 3.3 wt.% of nano-ZnO) and/or polyethylene glycol 6000 (20 wt.% of PEG 6000), without/with additional thermal modification at 190 °C/2 h. In the presence of nano-ZnO, the decay resistance of beech wood to the brown-rot fungus Rhodonia placenta and the white-rot fungus Trametes versicolor significantly increased, mainly after its additional thermal modification. The presence of nano-ZnO in beech wood—(a) alone, (b) with a subsequent application of PEG 6000, (c) with additional thermal modification—had a more apparent inhibition effect on T. versicolor than on R. placenta. PEG 6000 alone did not improve the resistance of beech wood to rot.
Various techniques of wood thermal modification in air, liquids, or melts at temperatures above 160 °C improve its resistance to biological damage and water. In this experiment, the European beech (Fagus sylvatica L.) wood was held for 1 to 4 hours in the melt of polyethylene glycol 6000 (PEG 6000) and during a given time either heated at 100 °C or thermally modified at 190 or 210 °C. Its decay resistance improved – maximally at using the more intense modification mode 210 °C/4h – to Poria placenta by 60.3% and to Trametes versicolor by 62.8%. The soaking and volume swelling in water of the PEG-thermally treated beech wood usually was significantly reduced, after 336 h maximally by 60% and 34.6%, respectively. The presence of PEG during the thermal modification processes caused darkening of beech wood – a decoratively interesting and more pronounced effect than what occurs in traditional air-thermal modifications – at which the Eab* was also great from 13.1 to 52.6. However, since the mechanical properties of the PEG-thermally modified beech wood worsened – impact bending strength maximally by 34% and Brinell hardness maximally by 43.3% – its application for structural elements would be limited.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.