The purpose of this article is to investigate the eff ect of sandblasting surface treatment, before the bonding process, on the strength of the adhesive joints of the three types of aluminium alloy sheets. Three values of pressure were used during the sandblasting process, i.e. 0.41 MPa, 0.51 MPa and 0.56 MPa. After mechanical treatment, the samples of aluminium alloys sheets were degreased three times with acetone by immersion. The elements were bonded with single-lap joints using two components epoxy adhesive. After the curing process, the shear strength tests of the aluminium alloy adhesive joints were conducted, according to the DIN EN 1465 standard. The surface topography of all samples was measured, and the most important surface roughness parameter and its waviness were determined. Based on the experimental results, it was noticed that, among others, while using the same pressure value during sandblasting of diff erent aluminium alloys, the roughness parameters Ra and Rz of the obtained surfaces diff ered depending on the type of alloy. It is also to notice that more than two times strength of the joints was obtained by those made of the aluminium alloy sheet, which was subjected to heat treatment.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.