Hot dipping Zn-Al-Mg coatings were prepared by rapid induction heating combined with gas protection. The influence of oxide scale on the structure and surface quality of a hot-dip Zn-6Al-3Mg alloy coating was studied in this paper. The results showed that the reaction of Fe-Al was suppressed by the scale on the surface of the steel plate. When the thickness of scale was 10 μm and the steel entry temperature was 900 °C, the surface quality of the coating was good. The Zn-Al-Mg coatings mainly consisted of the ternary eutectic structure of Zn/Al/MgZn2 and Fe4Al13 at the interface. When the scale thickness was 2–3 μm with the same steel entry temperature, the surface quality of the coating was poor, and serious stripe-like protrusion defects were formed on the surface of the coating, which was mainly caused by the Fe4Al13 phase separating from the substrate / coating interface into the overlay.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.