The formation of octonary DyErGdHoLuScTbY and senary DyGdHoLaTbY and ErGdHoLaTbY high-entropy alloys (HEAs) with the hexagonal close-packed (HCP) structure was reported in this study. Experiments using scanning electron microscopy and x-ray diffraction confirmed the single HCP solid solution in the as-cast state for these three HEAs if the presence of minor rare-earth oxides due to contamination from processing is ignored. The measured compressive yield stress values for these HEAs at room temperature are 245, 205, and 360 MPa for the ErGdHoLaTbY, DyGdHoLaTbY, and DyErGdHoLuScTbY HEAs, respectively. The corresponding solid solution strengthening contributions for these HEAs were estimated using a simple elastic model, and the resulting contributions were 28 MPa, 27 MPa, and 42 MPa for the three aforementioned HEAs.
[1.1]Silaferrocenophane 4, which contains pentacoordinate silicon moieties, was synthesized by the dimerization of 3 for the first time. The identity of 4 was established by multinuclear NMR spectroscopy, elemental analysis, and X-ray crystallography.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.