Background: Sulfur dioxide gas is known to include pollutants that are harmful to human health and the environment. Therefore, due to the increase of industrial activities, SO2 gas pollution control is very important. Objectives: The purpose of this study was to investigate the efficiency of sulfur dioxide removal by iron oxide nanoparticles deposited on clinoptilolite zeolite. Methods: Two materials, natural clinoptilolite and clinoptilolite containing iron oxide nanoparticles, were used as adsorbents of SO2. Both materials were characterized via scanning electron microscopy imaging, infrared spectroscopy, and N2 porosimetry, along with the determination of the thermodynamic properties and kinetics of SO2 adsorption. Therefore, breakthrough experiments were carried out at different temperatures and with different contact times. Sulfur dioxide adsorption of a real sample was considered for both adsorbents. Results: The adsorption efficiency of SO2 in the synthetic and actual sample was obtained at 80.3% and 66.7%, respectively, under optimum conditions (temperature of 25°C and duration of 28.5 minutes) by modified zeolite with iron oxide nanoparticles. The removal percentage average of SO2 was also obtained in the synthetic and actual sample at 43.8% and 31.3%, respectively, by zeolite in optimum conditions (temperature of 25°C and contact time of 20.5 minutes). The adsorption of SO2 with both adsorbents followed the pseudo-second-order equation and the adsorption process was an exothermic and spontaneous process. Conclusions: The addition of these iron oxide nanoparticles had a positive impact on the surface area and on SO2 capacity.
Introduction: The purpose of this study was to investigate and compare the effect of iron oxide nanoparticles on the adsorption of sulfur dioxide by modified zeolite with hydrochloric acid. In this investigation was used modi- fied zeolite with HCl with and without iron oxide nanoparticles (Iron Oxide Nanoparticles@Clinoptilolite/HCl) as adsorbent. Materials and methods: Structural characteristics, chemical composition and specific surface area of adsorbent were determined using the FTIR, FE- SEM, EDX, Mapping, XRD, XRF and BET techniques. Glass cylinder filled with zeolite seeds and SO2 cylinder balanced with N2 gas was used for experi- ments. It was evaluated factors affecting SO2 uptake process including tem- perature and contact time, also thermodynamics and kinetics of adsorption. Sulfur dioxide adsorption of real sample was taken with both adsorbents. Results: Adsorption efficiency of SO2 in the synthetic and actual sample were %82.8±5.5 and %67.2±7.21 respectively, by modified zeolite with HCl and iron oxide nanoparticles in the optimum conditions of temperature of 25 °C and duration 28.5 min. As well as, removal percentage average was obtained in the synthetic and actual sample %46.1±4.34 and %35.8±5.85 respectively, by modified zeolite with HCl without nanoparticles in optimum condition of temperature of 25 °C and contact time of 20.5 min.The results showed that SO2 adsorption is an exothermic and spontaneous process and adsorption ki- netics of sulfur dioxide by both adsorbent is more consistent Pseudo-second order kinetics model. Conclusion: The use of iron oxide nanoparticles on the zeolite can increase SO2 removal efficiency from the gas phase.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.