In order to effectively photodegradate organic pollutants, ZnO composite and Co-B codoped TiO2 films were successfully deposited on glass substrates via a modified sol-gel method and a controllable dip-coating technique. Combining with UV–Vis diffuse reflectance spectroscopy (DRS) and photoluminescence spectra (PL) analyses, the multi-modification could not only extend the optical response of TiO2 to visible light region but also decrease the recombination rate of electron-hole pairs. XRD results revealed that the multi-modified TiO2 film had an anatase-brookite biphase heterostructure. FE-SEM results indicated that the multi-modified TiO2 film without cracks was composed of smaller round-like nanoparticles compared to pure TiO2. BET surface area results showed that the specific surface area of pure TiO2 and the multi-modified TiO2 sample was 47.8 and 115.8 m2/g, respectively. By degradation of formaldehyde and oxytetracycline, experimental results showed that the multi-modified TiO2 film had excellent photodegradation performance under visible light irradiation.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.