Self-aligned inversion-channel In0.53Ga0.47As metal-oxide-semiconductor field-effect-transistors (MOSFETs) have been fabricated using the gate dielectrics of in-situ directly atomic-layer-deposited (ALD) HfO2 followed by ALD-Al2O3. There were no surface pretreatments and no interfacial passivation/barrier layers prior to the ALD. TiN/Al2O3 (4 nm)/HfO2 (1 nm)/In0.53Ga0.47As/InP MOS capacitors exhibited well-behaved capacitance-voltage characteristics with true inversion behavior, low leakage current densities of ∼10−8 A/cm2 at ±1 MV/cm, and thermodynamic stability at high temperatures. Al2O3 (3 nm)/HfO2 (1 nm)/In0.53Ga0.47As MOSFETs of 1 μm gate length, with 700 °C–800 °C rapid thermal annealing in source/drain activation, have exhibited high extrinsic drain current (ID) of 1.5 mA/μm, transconductance (Gm) of 0.84 mS/μm, ION/IOFF of ∼104, low sub-threshold swing of 103 mV/decade, and field-effect electron mobility of 1100 cm2/V · s. The devices have also achieved very high intrinsic ID and Gm of 2 mA/μm and 1.2 mS/μm, respectively.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.