Background The effect of nanofilled resin-based coating on the wear resistance of glass ionomer cements (GICs) is still controversial. This study aims to compare the wear resistance of four encapsulated GICs including two conventional and two resin-modified, and to evaluate the effect of G-Coat Plus on the wear resistance of GICs. Methods A total of 80 disk-shaped specimens were prepared from two CGICs (riva self cure (SDI) and Equia Forte Fil (GC) and two RM- GICs (Ketac Nano (3 M/ESPE) and Fuji II LC (GC). The specimens of each material were divided into two groups (n = 10) based on the surface protection: no coating (NC), and coating with G-Coat Plus (GCP). All specimens were then placed in distilled water for 24 h at 37 °C. The specimens were subjected to thermocycling for 120,000 cycles using a chewing simulator. Wear resistance was measured using a specific formula. Data was analyzed using Kruskal–Wallis test. Results There was no significant difference in volume loss (mm3) between coated and uncoated groups for all materials (P > 0.05). Ketac Nano showed significantly lower volume loss (0.65 ± 0.12) compared to all other groups (P < 0.05) among uncoated specimen, and significantly lower than Fuji II LC (P = 0.035) and Equia Forte Fil (P = 0.040) among coated groups. However, no statically significant difference was observed between volume loss of coated Ketac Nano with that of riva self cure (P = 0.087). Conclusions Coating with GCP did not affect the wear depth of GICs, and Ketac Nano showed significantly lower volume loss regardless of coating.

Background. The effect of nanofilled resin based coating on the wear resistance of glass ionomer cements (GICs) is still controversial. This study aims to compare the wear resistance of four encapsulated GICs including two conventional and two resin-modified, and to evaluate the effect of G-Coat Plus on the wear resistance of GICs. Methods. A total of 80 disk-shaped specimens were prepared from two CGICs (riva self cure (SDI) and Equia Forte Fil (GC) and two RM- GICs (Ketac Nano (3M/ ESPE) and Fuji II LC (GC). The specimens of each material were divided into two groups (n = 10) based on the surface protection: no coating (NC), and coating with G-Coat Plus (GCP). All specimens were then placed in distilled water for 24 h at 37 ºC. The specimens were subjected to thermocycling for 120,000 cycles using a chewing simulator. Wear resistance was measured using a specific formula. Data was analyzed using Kruskal-Wallis test. Results. There was no significant difference in volume loss (mm3) between coated and uncoated groups for all materials (P > 0.05). Ketac Nano showed significantly lower volume loss (0.65 ± 0.12) compared to all other groups (P < 0.05) among uncoated specimen, and significantly lower than Fuji II LC (P = 0.035) and Equia Forte Fil (P = 0.040) among coated groups. However, no statically significant difference was observed between volume loss of coated Ketac Nano with that of riva self cure (P = 0.087). Conclusions. Coating with GCP did not affect the wear depth of GICs, and Ketac Nano showed significantly lower volume loss regardless of coating.