The crystallite orientation and crystallographic domain structure of poly(ethylene oxide) (PEO) in cellulose nanofiber-incorporated (CNF-incorporated) PEO films developed for packaging materials were observed using wide-angle X-ray diffraction for different CNF filling ratios. When a CNF filling ratio of <10 wt % was used, the molecular chains in the PEO crystallite region were oriented in a direction perpendicular to the surface of the film; however, when the ratio was >50 wt %, the PEO molecular chains were oriented in a direction parallel to the surface of the film. The fiber axis of the CNFs became parallel to the surface of the PEO/CNF composite film when the filling ratio was >25 wt %. The change in the orientation of the PEO crystals occurred because increasing the amount of CNF in the composite films decreased the space in which the PEO could be crystallized. Furthermore, the hydrogen bonds between the PEO and the CNF may behave as crystallization nuclei for the PEO. Our results thus pave the way toward the development of packaging materials that are more impermeable to gases than the current materials.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.