This study is concerned with the microstructural analysis and improvement of the hardness and wear resistance of Ti-6Al-4V surface-alloyed materials fabricated by a high-energy electron beam. The mixtures of TiC, TiN, or TiC ϩ TiN powders and CaF 2 flux were deposited on a Ti-6Al-4V substrate, and then the electron beam was irradiated on these mixtures. In the specimens processed with a flux addition, the surface-alloyed layers of 1 mm in thickness were homogeneously formed without defects and contained a large amount (over 30 vol pct) of precipitates such as TiC, TiN, (Ti x Al 1Ϫx )N, and Ti(C x N 1Ϫx ) in the martensitic or N-rich acicular ␣ -Ti matrix. This microstructural modification, including the formation of hard precipitates and hardened matrices in the surface-alloyed layers, improved the hardness and wear resistance. Particularly in the surface-alloyed material fabricated by the deposition of TiN powders, the wear resistance was greatly enhanced to a level 10 times higher than that of the Ti alloy substrate. These findings suggested that surface alloying using high-energy electron-beam irradiation was economical and useful for the development of titanium-based surfacealloyed materials with improved hardness and wear resistance.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.