The lack of renewable resources and their inefficient use is a major challenge facing the society. Lignin is a natural biopolymer obtained mainly as a by-product from pulp-and paper-making industry, and is primarily burned to produce energy. However, the interest for using lignin in more advanced applications has increased rapidly. In particular, lignin based nanoparticles could find potential use in functional surface coatings, nanoglues, drug delivery, and microfluidic devices. In this work, a straightforward method to produce lignin nanoparticles from waste lignin obtained from kraft pulping is introduced.Spherical lignin nanoparticles were obtained by dissolving soft wood kraft lignin in tetrahydrofuran (THF) and subsequently introducing water into the system through dialysis. No chemical modification of the lignin was needed. Water acts as a nonsolvent reducing lignin's degrees of freedom causing the segregation of hydrophobic regions to compartments within the forming nanoparticles. The final size of the nanoparticles depended on the pre-dialysis concentration of dissolved lignin. The stability of the nanoparticle dispersion as a function of time, salt concentration and pH was studied. In pure water and room temperature the lignin nanoparticle dispersion was stable for over two months, but very low pH or high salt concentration induced aggregation. It was further demonstrated that the surface charge of the particles could be reversed and stable cationic lignin nanoparticles were produced by adsorption of poly(diallyldimethylammonium chloride) (PDADMAC).

In this study, tall oil fatty acid ester of softwood kraft lignin (TOFA-L) was used to prepare TOFA lignin nanoparticles (TLNP) in water. The average diameters for two prepared TLNPs in 0.1 mg/ ml concentration were 140 nm and 160 nm. TLNPs were attached covalently onto modified and unmodified cellulose fibres to form an antimicrobial composite material. The modified cellulose fibres contained reactive allylic double bonds with a degree of substitution of 0.05. The antimicrobial properties of both TLNPs and TLNP coated fibres (TLNP-C) were studied against Escherichia coli, Staphylococcus aureus and Pseudomonas aeruginosa using silver nanospheres (average size 10 nm) and Lignoboost lignin particles with 300 and 400 nm sizes as references. Antimicrobial activity of the samples was stronger against Gram-positive S. aureus cells than against Gram-negative target microbes E. coli and P. aeruginosa.