Highly transparent thin films with the chemical formula BaSrMgWO6 were deposited by spin coating using a solution of nitrates of Ba, Sr, and Mg and ammonium paratungstate in dimethylformamide with a Ba:Sr:Mg:W ratio = 1:1:1:1. XRD, SEM, EDX, and XPS investigations evidenced that annealing at 800 °C for 1 h results in an amorphous structure having a precipitate on its surface, and that supplementary annealing at 850 °C for 45 min forms a nanocrystalline structure and dissolves a portion of the precipitates. A textured double perovskite cubic structure (61.9%) was found, decorated with tetragonal and cubic impurity phases (12.7%), such as BaO2, SrO2, and MgO, and an under-stoichiometric phase (24.4%) with the chemical formula Ba2−(x+y) SrxMgyWO5. From transmittance measurements, the values of the optical band gap were estimated for the amorphous (Egdir = 5.21 eV, Egind = 3.85 eV) and nanocrystalline (Egdir = 4.69 eV, Egind = 3.77 eV) phases. The presence of a lattice disorder was indicated by the high Urbach energy values and weak absorption tail energies. A decrease in their values was observed and attributed to the crystallization process, lattice strain diminution, and cation redistribution.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.