This article presents the microstructure (SEM) and corrosion behavior of ZnAl12Mg3Si0.3 (ZAMS) coatings obtained by the double hot-dip method on Sebisty steel with increased strength. On the basis of chemical composition studies in micro-areas (EDS) and phase composition studies (XRD), structural components of the coating and corrosion products formed on the coating surface after exposure to the neutral salt spray (NSS) test (EN ISO 9227) were identified. The presence of the Fe(Al,Si,Zn)3 intermetallic phase was found in the Fe-Al intermetallic layer, while in the outer layer, dendrites rich in Al and Zn were identified. In these dendrites, the eutectics of Zn/MgZn2 and precipitates of the MgZn2 phase and Si were located. The NSS test showed better corrosion resistance of ZAMS coatings compared to conventional zinc hot-dip coatings. The increase in corrosion resistance is due to the formation of favorable corrosion products: simonkolleite—Zn5(OH)8Cl2·H2O and hydrozincite—Zn5(OH)6(CO3)2, and the presence of the MgZn2 phase in the coating, which is more anodic than other structural components.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.