Corrosion of built-in steel reinforcement ranks among the most serious mechanisms of bridge structure degradation. There are many reasons for the corrosion to occur: failures occurring during the bridge construction, consequences of traffic load, or, simple, ageing of the structures. Visual inspection of a bridge provides general information on the bridge condition. However, it cannot provide any information on the internal structure and integrity of the reinforced concrete or pre-loaded elements of the bridge in question. This is why non-destructive diagnostic methods are acquiring growing importance, helping researchers to properly evaluate the condition of a bridge and decide upon the most convenient methods for maintenance, repair or refurbishment of the bridge in question or its parts and schedule them accordingly.In this domain, methods employing the non-linear acoustic spectroscopy (NEWSNonlinear Elastic Wave Spectroscopy) achieved rush advancement recently. They are based on the fact that a non-linearity, which is due to the presence of a defect, makes an extraordinary indicator of the structure damage. These new, non-destructive methods appear to be promising for application to a wide range of materials featuring relatively heavy non-homogeneities, and for a large span of sites, from micro-chip to bridge structures. The present paper deals with an experimental study of the application of non-linear ultrasonic spectroscopy methods to the detection of steel reinforcement corrosion and its consequences for reinforced concrete specimens subjected to corrosion induced degradation cycles.
Non Destructive Testing is a powerful tool for determination of properties, durability and lifetime of concrete structures. Acoustic Emission Method is an unusual technique which describes only active defects or changes into structure arising as a consequence dangerous tension into structure. The method is appropriate to be used in homogenous structures as metal structures when cracks are highly active (generates sound). Its application in civil engineering is not so much used because building structures are inhomogeneous. This article shows possible application of Acoustic Emission Method for monitoring of concrete structure changes during its lifetime. The main aim of the article is to show the application of Acoustic Emission Method during the early age to 28 days after mixing. It is believed that early age of concrete structure is very important for its quality. Common concrete cube specimens have been tested after the production by Acoustic Emission Method with using waveguides. The results of acoustic emission method will be compared to classical parameters of fresh concrete e.g. the value water-cement ratio, air void content measured by different methods (pressure methods, AVA) and similar. In the results will be compared four mixtures when two mixtures were aerated and two mixtures were without aeration.
The aim of this paper is to evaluate the possibility of using the impact-echo method for monitoring extremely long-term frost resistance of ceramic tiles. Non-destructive testing methods make it possible to sensitively identify the occurrence and development of defects in materials. Impact-echo methods belong to the family of non-destructive testing methods and can be applied in many branches, among others also in civil engineering. To assess the ceramic-tile frost resistance, a new measurement method was developed based on using the acoustic properties of ceramic tiles. Sets of ceramic tiles of the Ia class were analyzed according to the EN 14 411 B standard. The ceramic tiles under investigation were subjected to degradation due to 500 freezethaw cycles in compliance with the relevant EN ISO 10545-12 standard. To verify the correctness of the impact-echo-method results, additional physical properties of the tested ceramic tiles were measured. To analyze the specimen-surface condition, we also used an Olympus LEXT 3100 confocal scanning microscope. It was proved that the impact-echo acoustic method is a sensitive indicator of a structure condition and can be applied to assess the frost resistance of a ceramic cladding element and predict its service life. Keywords: impact-echo, ceramic tiles, frost resistance, confocal microscopy, freeze-thaw cycles Namen tega~lanka je oceniti mo`nosti za uporabo metode Impact-echo za kontrolo ekstremno dolge odpornosti kerami~nih plo{~ic proti zmrzali. Neporu{ne preiskovalne metode omogo~ajo selektivno identifikacijo pojava in napredovanja napak v materialu. Metoda Impact-echo pripada skupini neporu{nih metod preiskav in je uporabna v mnogih bran`ah, med drugim tudi v gradbeni{tvu. Za oceno odpornosti kerami~nih plo{~ic je bila razvita nova merilna metoda, ki temelji na akusti~nih lastnostih kerami~nih plo{~ic. Analizirani so bili kompleti kerami~nih plo{~ic kvalitete Ia po standardu EN 14 411 B. Preiskovane kerami~ne plo{~ice so bile izpostavljene degradaciji pri 500 ciklih zamrznitve-odtaljevanja skladno z odgovarjajo~im standardom EN ISO 10545-12. Za preverjanje ustreznosti rezultatov metode Impact-echo so bile izmerjene dodatne fizikalne lastnosti kerami~nih plo{~ic. Za analizo stanja povr{ine vzorca je bil uporabljen konfokalni vrsti~ni mikroskop Olympus LEXT 3100. Dokazano je bilo, da je akusti~na metoda Impact-echo ob~utljiv pokazatelj stanja konstrukcije in je uporabna za ugotavljanje odpornosti proti zmrzovanju kerami~nih plo{~ic in za napovedovanje trajnostne dobe plo{~ic. Klju~ne besede: Impact-echo, kerami~ne plo{~ice, odpornost proti zmrzovanju, konfokalna mikroskopija, cikli zmrzovanje-odtaljevanje
This paper is focused on failure monitoring in lightweight concrete (special high-performance concrete that contains porous aggregate with a low bulk density) with high-strength polypropylene fibers under mechanical loading. The aim was to determine how the cracks' generation intensity in the tested concrete samples depends on the fibers' length and quantity. Our diagnostic method is based on a measurement of the acoustic and electromagnetic emission signals, which occur when solid dielectric materials are mechanically stressed. Several groups of lightweight concrete samples with various types and concentrations of high-strength polypropylene fibers were prepared for our experiment. We made two-channel measurements of the concrete samples from each group for defined loading conditions. The first channel was electromagnetic emission (EME) and the second was acoustic emission (AE). The electromagnetic emission and acoustic emission methods are promising methods to study the generation and behavior of cracks. The main advantage of EME and AE is their ability to be detected already in the stressed stage, which prevents macroscopic deterioration in solids. From the obtained results it can be concluded that the generated cracks' intensity is significantly affected by the presence of polypropylene fibers and by their length and dosage. Keywords: acoustic emission, electromagnetic emission, lightweight concrete, fiberŝ lanek je usmerjen na pregled po{kodb pri mehanskem obremenjevanju lahkega betona (poseben visoko zmogljiv beton, ki vsebuje porozne sestavine z majhno gostoto), z visokotrdnostnimi polipropilenskimi vlakni. Namen je bil ugotoviti, kako je intenziteta nastanka razpok odvisna od dol`ine in koli~ine vlaken. Diagnosti~na metoda je temeljila na merjenju akusti~nih signalov in signalov elektromagnetne emisije, ki se pojavijo kadar je trden dielektri~ni material mehansko obremenjen. Za eksperiment je bilo pripravljenih ve~vrst lahkih betonov z razli~no vrsto in koncentracijo visokotrdnostnih polipropilenskih vlaken. Pri dolo~enih pogojih obremenitve smo izvr{ili dvokanalne meritve vzorcev betona iz vsake skupine. Prvi kanal je bila elektromagnetna emisija (EME), drugi pa akusti~na emisija (AE). Metodi elektromagnetne emisije in akusti~ne emisije sta obetajo~i metodi za {tudij nastanka in obna{anja razpok. Glavna prednost EME in AE je, da ju je mogo~e odkriti`e med stanjem napetosti, kar prepre~i lokalne makroskopske po{kodbe v trdnem stanju. Iz dobljenih rezultatov je mogo~e zaklju~iti, da je intenzivnost nastajanja razpoke mo~no odvisna od prisotnosti polipropilenskih vlaken, od njihove dol`ine in odmerka. Klju~ne besede: akusti~na emisija, elektromagnetna emisija, lahki beton, vlakna
The aim of this paper is to evaluate the possibility of using the Impact-echo method for assessment of extremely long period of frost resistance of ceramic tiles. Sets of ceramic tiles of the Ia class to EN 14 411 B standard made by manufacture RACOs have been analyzed. The ceramic tiles under investigation have been subjected to 500 freeze-thaw-cycle based degradation in compliance with the relevant EN ISO 10545-12 standard. To verify the correctness of the Impact-echo method results, additional physical properties of the ceramic tiles under test have been measured. To analyze the specimen surface condition, we also used Olympus LEXT 3100 confocal scanning microscope. It has been proved that the acoustic method Impact-echo is a sensitive indicator of the structure condition and can be applied to the ceramic cladding element frost resistance and service life prediction assessment.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.