Nitrogen-containing carbon nanotubes (NCNTs) were prepared via pyrolysis of acetonitrile over cobalt catalysts at different temperatures to control the nitrogen content. The changes in the chemical and structural properties of undoped CNTs and NCNTs were investigated using high-resolution X-ray photoelectron and Raman spectroscopy. The NCNTs prepared at 550°C had a higher amount of pyridinic groups and edge plane exposure than the ones prepared at 750°C. The thermal stability and transformation of these nitrogen functional groups was studied using deconvoluted XP N 1s spectra. The NCNTs show a considerably higher activity in the oxygen reduction reaction in acidic electrolyte compared with undoped CNTs as demonstrated by cyclic voltammetry, rotating disk electrode measurements, and the redox-competition mode of scanning electrochemical microscopy (RC-SECM). Particularly, the NCNT sample prepared at 550°C exhibited the highest activity, which was about 1 order of magnitude lower than that of a commercial Pt/C sample containing 20 wt % Pt. The oxygen reduction reaction (ORR) performance of this sample showed hardly any signs of deterioration after 3 days, as determined by voltammetric stability tests in H 2 SO 4 .
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.