A comprehensive experimental and theoretical study of both thermal-induced spin transition (TIST) as a function of pressure and pressure-induced spin transition (PIST) at room temperature for the two-dimensional Hofmann-like SCO polymer [Fe(Fpz) 2 Pt(CN) 4 ] is reported. The TIST studies at different fixed pressures have been carried out by magnetic susceptibility measurements, while PIST studies have been performed by means of powder X-ray diffraction, Raman, and visible spectroscopies. A combination of the theory of elastic interactions and numerical Monte Carlo simulations has been used for the analysis of the cooperative interactions in TIST and PIST studies. A complete ( T , P ) phase diagram for the compound [Fe(Fpz) 2 Pt(CN) 4 ] has been constructed. The critical temperature of the spin transition follows a lineal dependence with pressure, meanwhile the hysteresis width shows a nonmonotonic behavior contrary to theoretical predictions. The analysis shows the exceptional role of the total entropy and phonon contribution in setting the temperature of the spin transition and the width of the hysteresis. The anomalous behavior of the thermal hysteresis width under pressure in [Fe(Fpz) 2 Pt(CN) 4 ] is a direct consequence of a local distortion of the octahedral geometry of the Fe(II) centers for pressures higher than 0.4 GPa. Interestingly, there is not a coexistence of the high- and low-spin (HS and LS, respectively) phases in TIST experiments, while in PIST experiments, the coexistence of the HS and LS phases in the metastable region of the phase transition induced by pressure is observed for a first time in a first-order gradual spin transition with hysteresis.

No abstract

Two types of experiments conducted to investigate the effect of pressure on the spin crossover (SCO) properties of the 2D Fe­(II) coordination polymer formulated {Fe­[bipy­(ttr)2]} n are reported, namely, (1) magnetic measurements performed at variable temperature and at fixed pressure and (2) visible spectroscopy at variable pressure and fixed temperature. The magnetic experiments carried out under a hydrostatic pressure constraint of 0.04, 0.08, and 0.8 GPa reveal a two-step spin transition behavior. The characteristic critical temperatures of the spin transition are shifted upward in temperature as pressure increases. The slope of the straight-line of the T c vs P plot, dT c/dP, is 775 K/GPa and 300 K/GPa, for the high temperature and the low temperature steps, respectively. These values are remarkably large and denote the extreme sensitivity of the material to the application of pressure. Indeed, the visible spectroscopic measurements performed at 293 K show that a complete spin transition is induced at pressures as low as 0.4 GPa. Moreover, the pressure-induced spin transition is reversible and shows an asymmetric hysteresis. An analysis of the cooperative interactions of the thermal- and pressure-induced spin transition in the framework of the model of elastic interactions reveals that the elastic energy of the lattice as well as the interaction parameter between the SCO centers change during the course of the spin transition. Consequently, the character of the spin transition varies from abrupt for the high temperature step to continuous for the low temperature step.

No abstract