Metal–organic frameworks (MOFs)-derived materials with a large specific surface area and rich pore structures are favorable for catalytic performance. In this work, MOFs are successfully prepared. Through pyrolysis of MOFs under nitrogen gas, zinc-based catalysts with different active sites for acetylene acetoxylation are obtained. The influence of the oxygen atom, nitrogen atom, and coexistence of oxygen and nitrogen atoms on the structure and catalytic performance of MOFs-derived catalysts was investigated. According to the results, the catalysts with different catalytic activity are Zn-O-C (33%), Zn-O/N-C (27%), and Zn-N-C (12%). From the measurements of X-ray photoelectron spectroscopy (XPS), it can be confirmed that the formation of different active sites affects the electron cloud density of zinc. The electron cloud density of zinc affects the ability to attract CH3COOH, which makes catalysts different in terms of catalytic activity.

The role of solvents is crucial in catalyst preparation. With regard to catalysts prepared with activated carbon (AC) as the carrier, when water is used as a solvent it is difficult for the solution to infiltrate the AC. Because AC comprises a large number of C atoms and is a nonpolar material, it is more effective for the adsorption of nonpolar substances. Since the water and active ingredients are polar, they cannot easily infiltrate AC. In this study, the dispersion of the active component was significantly improved by optimizing the solvent, and the particle size of the active component was reduced from 33.08 nm to 15.30 nm. The specific surface area of the catalyst is significantly increased, by 10%, reaching 991.49 m2/g. Under the same reaction conditions, the conversion of acetic acid by the catalyst prepared with the mixed solvent was maintained at approximately 65%, which was 22% higher than that obtained using the catalyst prepared with water as the solvent.

The preparation method and calcination temperature of metal-organic framework (MOFs)-derived materials are critical factors affecting catalytic performance. In this work, the preparation conditions of MOFS precursors were optimized, and zinc-based catalysts with different activities (MOF5-700, MOF5-750, and MOF5-800) were obtained by pyrolysis of MOFS precursors under nitrogen, which were then applied to an acetylene acetoxylation reaction system. According to the results, the conversion rate of acetic acid under catalysis was significantly different. (MOF5-700 (48%), MOF5-750 (62%), and MOF5-800 (22%)). Comparing the activity of the catalyst with the industrial catalyst Zn(OAc)2/AC (20%), MOF5-750 showed higher activity, and the acetic acid conversion rate remained around 60% after 50 h of stability testing. By characterization analysis, MOFs-derived materials were obtained after proper temperature pyrolysis. They have high mesoporous content, defects, and oxygen-containing functional groups and can maintain a good crystal structure, greatly reducing the loss of active components. This is the main reason for the good performance of the MOF5-750 catalyst in acetylene acetoxylation. Thus, the preparation conditions and favorable pyrolysis temperature of MOF derivative catalysts play a key role in the catalytic performance of acetylene acetoxylation.