Silica sodalite was obtained using topotactic conversion of layered silicate RUB-15 through stepwise processes that consisted of the control of stacking sequence of the layers, interlayer condensation by refluxing, and elimination of intercalated guest species. The interlayer condensation of RUB-15, in which acetic acid was pre-intercalated between the layers to control the stacking sequence, afforded a sodalite framework containing organic guest species by refluxing in N-methylformamide (NMF). The pre-intercalated acetic acid molecules were largely replaced with NMF. This formation process of silica sodalite containing large amounts of intercalated organic guest species is in clear contrast to the previously reported process that used direct calcination of an intercalation compound of layered RUB-15 accommodating acetic acid between the layers. Calcination of the condensed product provided sodalite with fewer defects than the directly calcined product, thus indicating the advantage of the stepwise process. The method reported here is useful for the preparation of pure silica sodalite with relatively low defects and plate-like morphology.
Silicate nanoscrolls with crystalline walls were prepared by intercalation of layered octosilicate with organoammonium ions and the subsequent solvothermal treatment.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.