Bone tissue engineering mandates the development of a functional scaffold that mimics the physicochemical properties of native bone. Bioglass 45S5 (BG) is a highly bioactive material known to augment bone formation and restoration. Hybrid scaffolds fabricated using collagen type I and BG resemble the organic and inorganic composition of the bone extracellular matrix and hence have been extensively investigated for bone tissue engineering applications. However, collagen-BG scaffolds developed thus far do not recapitulate the aligned structure of collagen found in native bone. In this study, an electrochemical fabrication method was employed to synthesize BG-incorporated electrochemically aligned collagen (BG-ELAC) threads that are compositionally similar to native bone. Further, aligned collagen fibrils within BG-ELAC threads mimic the anisotropic arrangement of collagen fibrils in native bone. The effect of BG incorporation on the mechanical properties and cell-mediated mineralization on ELAC threads was investigated. The results indicated that BG can be successfully incorporated within ELAC threads, without disturbing collagen fibril alignment. Further, BG incorporation significantly increased the ultimate tensile stress (UTS) and modulus of ELAC threads (p < 0.05). SBF conditioning showed extensive mineralization on BG-ELAC threads that increased over time demonstrating the bone bioactivity of BG-ELAC threads. Additionally, BG incorporation into ELAC threads resulted in increased cell proliferation (p < 0.05) and deposition of a highly dense and continuous mineralized matrix. In conclusion, incorporation of BG into ELAC threads is a viable strategy for the development of an osteoconductive material for bone tissue engineering applications. © 2017 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 105A: 2429-2440, 2017.

Plastic compression is a collagen densification process that has been widely used for the development of mechanically robust collagen-based materials. Incorporation of bioglass within plastically compressed collagen gels has been shown to mimic the microstructural properties of native bone and enhance in vitro cell-mediated mineralization. The current study seeks to decouple the effects of collagen densification and bioglass incorporation to understand the interplay between collagen packing density and presence of bioglass on cell-mediated mineralization. Saos-2 cell-mediated mineralization was assessed as a measure of the osteoconductivity of four different collagen gels: (1) uncompressed collagen gel (UC), (2) bioglass incorporated uncompressed collagen gel (UC + BG), (3) plastically compressed collagen gel (PC), and (4) bioglass incorporated plastically compressed collagen gel (PC + BG). The results indicated that collagen densification enhanced mineralization as shown by SEM, increased alkaline phosphatase activity and produced significantly higher amounts of mineralized nodules on PC gels compared to UC gels. Further, the amount of nodule formation on PC gels was significantly higher compared to UC + BG gels indicating that increase in matrix stiffness due to collagen densification had a greater effect on cell-mediated mineralization compared to bioglass incorporation into loosely packed UC gels. Incorporation of bioglass into PC gels further enhanced mineralization as evidenced by significantly larger nodule size and higher amount of mineralization on PC + BG gels compared to PC gels. In conclusion, collagen densification via plastic compression improves the osteoconductivity of collagen gels. Further, incorporation of bioglass within PC gels has an additive effect and further enhances the osteoconductivity of collagen gels.