Nano technology is the science and engineering related to particles sized 10-9 of a meter. Albeit, the small size, they have opened up a huge array of possibilities for this world. By the inclusion of nanoparticles in various materials not only, the field of engineering but also, medical and dentistry have been benefitted largely. Researchers have manipulated the particles at a molecular and atomic level, which have opened up huge possibilities for the same material. The recent advances have helped to achieve accurate and fast diagnosis, helped to prolong the longevity of dental materials and hence helped to create a healthy oral environment. However, with all these developments, it is important that we focus on the shortcoming or the hazards too and carefully comply with the same before its long-term application. Therefore, this article focuses on the basis, all the present applications of Nano dentistry and the potential it holds for the field of dentistry in future.
Background. To evaluate and compare the shear bond strength of feldspathic porcelain to four distinctively surface-treated Ni-Cr and Co-Cr alloys and to assess the impact of oxidation-heat treatment on porcelain to base metal alloy bond strength. Methods. 40 specimens each of nickel-chromium alloy and cobalt-chromium alloy were cast. A total of four groups of specimens were created. Group I was surface-treated by sandblasting with 50 μm alumina particles, Group II was surface-treated by sandblasting with 110 μm alumina particles, Group III and Group IV were surface-treated with 250 μm alumina particles. In Group IV, after sandblasting initially with 250 μm alumina particles, the alloys were subjected to oxidation and resandblasting with 250 μm alumina particles. Each of the specimen was coated with opaque and body porcelain and fired to a total thickness of 2 mm porcelain. A universal measuring machine was used to assess shear bond strength at a crosshead speed of 0.5 mm/min. Results. Two-way ANOVA followed by Tukey’s post hoc test was used to assess the significant difference within the groups. Unpaired t-test was used for the intergroup comparison of the obtained data. The study showed that the size of the air abrasion particles used for sandblasting significantly influenced the porcelain to metal surface bond strength, with p value <0.001. The bond strength values of the two alloys tested showed no major variations. Result also showed that oxidation influences the metal-ceramic bond strength. Conclusions. The bond strength of the metal-ceramic interface is influenced by the alloy’s surface treatment. The oxidation process impacts the bond strength of the metal-ceramic system.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.