Samples of the Al 7075 naturally and artificially aged were processed by conventional and asymmetrical rolling with 5% of thickness reduction. The rolling processes were evaluated under room temperature and under warm condition (130°C). Mechanical properties were evaluated by uniaxial tensile and Vickers microhardness tests. Microstructure evolutions were followed by optical microscopy analysis. Naturally aged samples showed better yield strengthening under warm processing. Greater ultimate stress and ductility under room temperature processing was also noticed in naturally aged specimens. Artificially aged samples showed better mechanical properties under room temperature, softening under warm processing due to grain recovery process. Microhardness tests showed expected results for both rolling types, especially on asymmetrical rolling with the higher predictions were observed. Micrographs have shown no expressive grain changes or refinement although its flattening was observed. Precipitates were analyzed by EDS/SEM revealing the presence of MgZn 2 and CuMgAl along the matrix that provides plastic strengthening.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.