For use as fuel cladding of liquid metal fast reactors, Fe-0.12C-9Cr-2W ODS martensitic steel claddings were developed by cold-rolling under the softened ferrite phase induced by slow cooling from austenite phase, subsequently by ferrite to austenite phase transformation to break up substantially elongated grains produced by cold-rolling at the final heat-treatment. The produced claddings showed noticeable improvement in tensile and creep rupture strength that are considerably superior to PNC-FMS and even austenitic PNC316 at higher temperature and extended time to rupture. The strength improvement is mainly attributed to titanium addition in ODS martensitic steels through its reduction of Y 2 O 3 particle size and shortening inter-particles spacing. The behavior of oxide particle size reduction is associated with stoichiometry between Y 2 O 3 and TiO 2 .

No abstract

The high temperature strengthening mechanism of previously manufactured 12Cr-ODS ferritic steel claddings was clarified. In the recrystallized 12Cr-2W-0.3Ti-0.24Y 2 O 3-ODS ferritic steel cladding, αY 2 TiO 5 type complex oxide formation was responsible for the drastic reduction of oxide particle size and the resulting shortened distance between particles, which led to superior internal creep rupture strength at 973 K because of the high resistance to gliding dislocation. Internal creep deformation was considered to be controlled by the grain boundary sliding associated with grain morphology: the near 11, 9 and 19 coincidence boundaries with a 110 common axis.

No abstract