Infrared-to-visible upconversion phosphors (i.e., rare earth ion-doped Y2O3 nanoparticles (UNPs)) were synthesized by the homogeneous precipitation method. Because the charge on the erbium (Er) ion-doped Y2O3 (Y2O3:Er) NP (UNP1) surface is positive under neutral conditions, the UNP1 surface was electrostatically PEGylated using negatively charged poly(ethylene glycol)- b-poly(acrylic acid) (PEG- b-PAAc). The adsorption of PEG- b-PAAc was confirmed by Fourier transform infrared (FT-IR) measurements and thermal gravimetric analysis (TGA). The surface charge of the PEGylated UNP1s (PEG-UNP1s) was effectively shielded by the PEGylation. The dispersion stability of the UNP1s was also significantly improved by the PEGylation. The PEG-UNP1s were dispersed over 1 week under physiological conditions as a result of the steric repulsion between the PEG chains on the UNP1 surface. The upconversion emission spectrum of PEG-UNP1s was observed under physiological conditions and was confirmed by near-infrared excited fluorescence microscope observation. Streptavidin (SA)-installed ytterbium (Yb) and Er ion-codoped Y2O3 (Y2O3:Yb,Er) NPs (UNP2s) were prepared by the coimmobilization of PEG- b-PAAc and streptavidin. The PEG/SA coimmobilized UNP2s (PEG/SA-UNP2s) specifically recognized biotinylated antibodies and emitted strong upconversion luminescence upon near-infrared excitation. The obtained PEG/streptavidin coimmobilized UNPs are promising as high-performance near-infrared biolabeling materials.

A novel ratiometric nanothermometer based on over-1000 nm near-infrared emission of rare-earth doped ceramic nanophosphors was developed for temperature measurement.

Therapeutic efficacy of glioblastoma multiforme (GBM) is often severely limited by poor penetration of therapeutics through blood-brain barrier (BBB) into brain tissues and lack of tumor targeting. In this regard, a functionalized upconversion nanoparticle (UCNP)-based delivery system which can target brain tumor and convert deep tissue-penetrating near-infrared (NIR) light into visible light for precise phototherapies on brain tumor was developed in this work.Methods: The UCNP-based phototherapy delivery system was acquired by assembly of oleic acid-coated UCNPs with angiopep-2/cholesterol-conjugated poly(ethylene glycol) and the hydrophobic photosensitizers. The hybrid nanoparticles (ANG-IMNPs) were characterized by DLS, TEM, UV/vis and fluorescence spectrophotometer. Cellular uptake was examined by laser scanning confocal microscopy and flow cytometry. The PDT/PTT effect of ANG-IMNPs was evaluated using MTT assay. Tumor accumulation of NPs was determined by a non-invasive in vivo imaging system (IVIS). The in vivo anti-glioma effect of ANG-IMNPs was evaluated by immunohistochemical (IHC) examination of tumor tissues and Kaplan-Meier survival analysis.Results: In vitro data demonstrated enhanced uptake of ANG-IMNPs by murine astrocytoma cells (ALTS1C1) and pronounced cytotoxicity by combined NIR-triggered PDT and PTT. In consistence with the increased penetration of ANG-IMNPs through endothelial monolayer in vitro, the NPs have also shown significantly enhanced accumulation at brain tumor by IVIS. The IHC tissue examination confirmed prominent apoptotic and necrotic effects on tumor cells in mice receiving targeted dual photo-based therapies, which also led to enhanced median survival (24 days) as compared to the NP treatment without angiopep-2 (14 days).Conclusion: In vitro and in vivo data strongly indicate that the ANG-IMNPs were capable of selectively delivering dual photosensitizers to brain astrocytoma tumors for effective PDT/PTT in conjugation with a substantially improved median survival. The therapeutic efficacy of ANG-IMNPs demonstrated in this study suggests their potential in overcoming BBB and establishing an effective treatment against GBM.

A novel poly(ethylene glycol) (PEG)-based block copolymer possessing a 4-vinylbenzylphosphonate repeating unit in another segment (PEG-block-poly(4-vinylbenzylphosphonate)) (PEG-b-PVBP) was designed and successfully synthesized. As a control, an end-functionalized PEG possessing a mono-phosphonate group (PEG-PO(3)H(2)) was also synthesized. The surface of near-infrared (NIR) phosphors (i.e., ytterbium (Yb) and erbium (Er) ion-codoped Y(2)O(3) nanoparticles (YNPs)) were modified with PEG-b-PVBP (PEG-YNP(b)s) and PEG-PO(3)H(2) (PEG-YNP(1)s). The adsorption of PEG-b-PVBP and PEG-PO(3)H(2) was estimated by Fourier transform infrared (FT-IR) measurements and thermal gravimetric analysis (TGA). The physicochemical characteristics of the obtained YNP samples were analyzed by ζ-potential and dynamic light scattering (DLS) measurements. The ζ-potentials of YNPs modified by these polymers were close to zero, indicating the effective coverage of the YNP surface by our new PEG derivatives. However, the dispersion stability of the PEGylated YNPs was strongly affected by the structure of the PEG terminus. The average diameter of the PEG-YNP(1)s increased, and aggregates precipitated after less than 1 h in phosphate buffer saline (PBS). In contrast, the size did not change at all in the case of PEG-YNP(b)s and the dispersion in PBS was stable for over 1 week. PEG-YNP(b)s also showed high erosion resistance under acidic conditions. The multiple coordinated PVBP segment of the block copolymer on the YNP surface plays a substantial role in improving such dispersion stability. The excellent dispersion stability and strong NIR luminescence of the obtained PEG-YNP(b)s were also confirmed in fetal bovine serum (FBS) solution over 1 week. Furthermore, in vivo NIR imaging of live mice was performed, and the 1550 nm NIR emission of PEG-YNP(b)s from the organ of live mice was confirmed without dissection.

A new family of block ionomer complexes (BIC) formed by poly(ethylene glycol)-block-poly(4-vinylbenzylphosphonate) (PEG-b-PVBP) and various cationic surfactants was prepared and characterized. These complexes spontaneously self-assembled in aqueous solutions into particles with average size of 40-60nm and remained soluble over the entire range of the compositions of the mixtures including stoichiometric electroneutral complexes. Solution behavior and physicochemical properties of such BIC were very sensitive to the structure of cationic surfactants. Furthermore, such complexation was used for incorporation of cationic anti-cancer drug, doxorubicin (DOX), into the core of BIC with high loading capacity and efficiency. The DOX/PEG-b-PVBP BIC also displayed high stability against dilution, changes in ionic strength. Furthermore, DOX release at the extracellular pH of DOX/PEG-b-PVBP BIC was slow. It was greatly increased at the acidic pH mimicking the endosomal/lysosomal environment. Confocal fluorescence microscopy using live MCF-7 breast cancer cells suggested that DOX/PEG-b-PVBP BICs are transported to lysosomes. Subsequently, the drugs are released and exert cytotoxic effect killing these cancer cells. These findings indicate that the obtained complexes can be attractive candidates for delivery of cationic drugs to tumors.

No abstract

Contactless thermal imaging generally relies on mid-infrared cameras and fluorescence imaging with temperature-sensitive phosphors. Fluorescent thermometry in the near-infrared (NIR) region is an emerging technique for analysing deep biological tissues but still requires observation depth calibration. We present an NIR fluorescence time-gated imaging (TGI) thermometry technology based on fluorescence lifetime, an intrinsic fluorophore time constant unrelated to observation depth. Fluorophore used is NaYF 4 co-doped with Nd 3+ and Yb 3+ that emits fluorescence at 1000 nm. An agarose gel-based phantom with the fluorophore embedded at a 5-mm depth was covered by sheets of meat to vary the observation depth. The temperature was determined independently from depth by sequences of NIR fluorescence decay images, and the rate of change in the fluorescence lifetime per temperature was almost constant (−0.0092 ~ −0.010 °C −1 ) at depths ranging from 0 to 1.4 mm of meat, providing non-contact and absolute measurements of temperature in deep biological tissues.

A method was developed for photocontrolling cell adhesion on a gel substrate with defined mechanical properties. Precise patterning of geometrically controlled cell clusters and their migration induction became possible by spatiotemporally controlled photo-irradiation of the substrate. The clusters exhibited unique collective motion that depended on substrate stiffness and cluster geometry.