Development of a technology for the synthesis of monometallic or multimetallic nanoparticles is exceptionally vital for the preparation of novel magnetic, optical. and catalytic functional materials. In this context, the polyol process is a safe and scalable method for preparation of metal nanoparticles with controlled sizes and shapes in large scales. However, there is no systematic investigation that discusses the criteria for the selection of metal salt and solvent type that determine the kinetics of reduction reaction that influences the morphology of the particles. Consequently, the design of metallic nanoparticles, which is controlled by the kinetics and thermodynamics of the reduction reaction, has become difficult. In this paper, the selection criterion for metal salt precursor is established based on the presumption that the ligand of the metal precursor promotes the formation of active species of the solvent, and the criterion for the selection of the solvent type is based on the highest occupied molecular orbital (HOMO) energy value estimated using molecular orbital theory. The results suggested that the dissociation constants of metal salt precursors and HOMO energy of the polyol solvent can be tuned to control the kinetics of the reduction reaction. The reduction potential of polyol depends on the number of carbon atoms and the location of hydroxyl ligands within the molecule. Among the polyols considered in this study, 1,4-butanediol had the highest reduction potential. The predictions have been experimentally verified by synthesizing metallic Co and Fe nanoparticles. The findings could be extended to other techniques such as thermal decomposition and alcohol reduction for the synthesis of noble metal-transition metal magnetic and catalytic nanoparticles with novel properties.

Recently, the development of bimetallic nanoparticles with functional properties has been attempted extensively but with limited control over their morphological and structural properties. The reason was the inability to control the kinetics of the reduction reaction in most liquid-phase syntheses. However, the alcohol reduction technique has demonstrated the possibility of controlling the reduction reaction and facilitating the incorporation of other phenomena such as diffusion, etching, and galvanic replacement during nanostructure synthesis. In this study, the reduction potential of straight-chain alcohols has been investigated using molecular orbital calculations and experimentally verified by reducing transition metals. The alcohols with a longer chain exhibited higher reduction potential, and 1-octanol was found to be the strongest among alcohols considered. Furthermore, the experimental evaluation carried out via the synthesis of metallic Cu, Ni, and Co particles was consistent with the theoretical predictions. The reaction mechanism of metallic particle formation was also studied in detail in the Ni–1-octanol system, and the metal ions were confirmed to be reduced via the formation of nickel alkoxide. The results of this investigation were successfully implemented to synthesize Cu–Ni bimetallic nanostructures (core–shell, wire, and tube) via the incorporation of diffusion and etching besides the reduction reaction. These results suggest that the designed synthesis of a wide range of bimetallic nanostructures with more refined control has become possible.

Bimetallic nanomaterials have attracted much attention from various fields such as catalysis, optics, magnetism, and so forth. The functionality of such particles is influenced very much by the intermetallic interactions than their individual contribution. However, compared with the synthesis of monometallic nanoparticles, the reaction parameters that need to be controlled for tuning the size, shape, composition, and crystal structure of bimetallic nanoparticles becomes challenging. This study focuses on synthesizing of bimetallic nanostructures using the alcohol reduction method, where the control over the reducing power is conceivable by varying the combination of the alcohol type, complexing agent, and metal salts. Consequently, various Cu−Co nanostructures such as Cu−Co core−shell (size ranged between 40 and 15 nm) and hollow alloy nanoparticles and nanotubes were successfully synthesized by incorporating diffusion and etching phenomena during the reduction reaction. Moreover, time-resolved sampling revealed that the formation of a Cu−Co alloy hollow nanostructure has been realized by the diffusion of the Cu core into the Co shell by controlling the reduction time gap between Cu and Co and the crystal structure besides the reduction sequences. It should be noted that the synthesis of a high-temperature (∼1300 °C) Cu−Co alloy phase was carried out at 170 °C. Among the Cu−Co alloy nanostructures, Cu−Co hollow alloy nanoparticles exhibited enhanced catalytic activity compared to metallic Cu and other Cu−Co nanostructures from the degradation reaction of methylene blue. The enhanced catalytic performance was considered to be mainly due to the alloy structure.

Development of a novel alcohol reduction technique for the one-pot synthesis of Cu–Ni NWs by elucidating the formation mechanism by using in situ spectroscopic measurements.