Hydrated ionic liquids (ILs) were prepared by adding appropriate amounts of water to hydrophilic ILs. Some hydrated ILs show excellent solubilizing ability for proteins, keeping the basic properties of ILs. The solubility of cytochrome c (cyt c) depended on the structure of the component ions. When component anions have oxo acid residues, the resulting hydrated ILs solubilize cyt c quite well. In such hydrated ILs, the structure and activity of cyt c is influenced by the kosmotropicity of the component ions. We synthesized ILs from various ions having different kosmotropicity, including dihydrogen phosphate (dhp), dibutylphosphate, acetate, lactate, and methanesulfonate as anions. The activity of the dissolved cyt c depends on the permutations of kosmotropicity of the component ions. cyt c shows no structural change and retains its activity when dissolved in the hydrated choline dhp, which is an excellent combination of chaotropic cation and kosmotropic anion. Furthermore, cyt c dissolved in the hydrated choline dhp remained in a native state and was active after 18 months of storage at room temperature.

A series of salts, some of which are ionic liquids, are prepared from cations and anions drawn from Active Pharmaceutical Ingredients (APIs) and Generally Recognized As Safe (GRAS) materials. Using the solid-state structures of the crystalline salts as a basis, an anti-crystal engineering approach to the preparation of “Active Ionic Liquids” (AILs) is explored.

Organic ionic plastic crystals (OIPCs) are a class of solid-state electrolytes with good thermal stability, non-flammability, non-volatility, and good electrochemical stability. When prepared in a composite with electrospun polyvinylidene fluoride (PVdF) nanofibers, a 1:1 mixture of the OIPC N-ethyl-N-methylpyrrolidinium bis(fluorosulfonyl)imide ([C mpyr][FSI]) and lithium bis(fluorosulfonyl)imide (LiFSI) produced a free-standing, robust solid-state electrolyte. These high-concentration Li-containing electrolyte membranes had a transference number of 0.37(±0.02) and supported stable lithium symmetric-cell cycling at a current density of 0.13 mA cm . The effect of incorporating PVdF in the Li-containing plastic crystal was investigated for different ratios of PVdF and [Li][FSI]/[C mpyr][FSI]. In addition, Li|LiNi Co Mn O cells were prepared and cycled at ambient temperature and displayed a good rate performance and stability.